Microstructure And Mechanical Property Improvement Of Dissimilar Metal Joints For Tc4 Ti Alloy To Nitinol Niti Alloy By Laser Welding

Yan Zhang,DeShui Yu,JianPing Zhou,DaQian Sun,HongMei Li
DOI: https://doi.org/10.1515/ijmr-2020-7935
2021-01-01
International Journal of Materials Research
Abstract:To avoid the formation of Ti-Ni intermetallics in a joint, three laser welding processes for Ti alloy-NiTi alloy joints were introduced. Sample A was formed while a laser acted at the Ti alloy-NiTi alloy interface, and the joint fractured along the weld centre line immediately after welding without filler metal. Sample B was formed while the laser acted on a Cu interlayer. The average tensile strength of sample B was 216 MPa. Sample C was formed while the laser acted 1.2 mm on the Ti alloy side. The one-pass welding process involved the creation of a joint with one fusion weld and one diffusion weld separated by the remaining unmelted Ti alloy. The mechanical performance of sample C was determined by the diffusion weld formed at the Ti alloy-NiTi alloy interface with a tensile strength of 256 MPa.Y
What problem does this paper attempt to address?