Abstract:A cerium (Ce)‐doped zinc oxide (ZnO) photocatalyst with abundant Ce‐O‐Zn units was developed, where Ce and Zn atoms serve as the photoreduction sites of carbon dioxide and photooxidation sites of methane, respectively. The close proximity of Ce and Zn atoms allowed to further efficiently couple the C1 intermediates into ethanol, with a peak rate of 580 μmol·g−1·h−1. Partial oxidation of methane (CH4) to value‐added products is significantly challenging due to the highly inert chemical property of CH4 at ambient conditions and easy over‐oxidation into carbon dioxide (CO2) or carbon monoxide (CO) at elevated temperatures and pressures. Targeting this challenge, the efficient photocatalytic coupling of CO2 and CH4 into ethanol is demonstrated, using a cerium (Ce)‐doped zinc oxide (ZnO) photocatalyst with abundant Ce─O─Zn units. Under light illumination, CO2 is adsorbed on the Ce atoms and photo‐reduced to CO, and CH4 is captured by the Zn atoms and photo‐oxidized to hydroperoxymethane (CH3OOH). The close proximity of Ce and Zn atoms on the Ce─O─Zn units allowed to further efficiently couple the as‐formed CO and CH3OOH into ethanol. Without additional Oxygen (O2) oxidant or sacrificial regent, the ethanol production rate reached 580 μmol g−1 h−1, substantially exceeding previously reports on photocatalytic CH4 oxidation. This work features to convert two greenhouse gases into value‐added chemicals with adjacent and asymmetric reaction sites, suggesting attractive potentials for CH4 and CO2 utilization.

CeO2 Supported Pd Dimers Boosting CO2 Hydrogenation to Ethanol

Efficiently Electroreducing CO2 to Ethylene on Heterostructured CeO2/CuO

Enhanced Selectivity of Phenol Hydrogenation in Low-Pressure CO2 over Supported Pd Catalysts

Highly dispersed Pd nanoparticles supported on dendritic mesoporous CeZrZnOx for efficient CO2 hydrogenation to methanol

Local In-O-Pd Lewis Acid-Base Pair Boosting CO2 Selective Hydrogenation to Methanol

PdCu supported on dendritic mesoporous CexZr1-xO2 as superior catalysts to boost CO2 hydrogenation to methanol

Roles of Hydroxyl and Oxygen Vacancy of CeO 2 ·xh 2 O in Pd-catalyzed Ethanol Electro-Oxidation

Boosting CO2 electrocatalytic reduction to ethylene via hydrogen-assisted C-C coupling on Cu2O catalysts modified with Pd nanoparticles

Ceo2/Cus Nanoplates Electroreduce Co2 to Ethanol with Stabilized Cu+ Species

Selective Hydrogenation of CO2 to Ethanol over Cobalt Catalysts

Catalytic Activity for CO2 Hydrogenation is Linearly Dependent on Generated Oxygen Vacancies over CeO2‐Supported Pd Catalysts

Simultaneously Promoted Water Resistance and CO2 Selectivity in Methanol Oxidation Over Pd/CoOOH: Synergy of Co-OH and the Pd-Olatt-Co Interface

Direct Conversion of CO 2 to Ethanol Boosted by Intimacy-Sensitive Multifunctional Catalysts

CO2 Hydrogenation to Methanol over Bimetallic Pd-Cu Catalysts Supported on TiO2-CeO2 and TiO2-ZrO2

Photocatalytic Coupling of CH4 and CO2 to Ethanol on Asymmetric Ce−O−Zn Sites

Boosting the Catalytic Performance of CuO x in CO 2 Hydrogenation by Incorporating CeO 2 Promoters

CO2 hydrogenation to methanol over PdZn catalysts on bimetallic modified dendritic mesoporous silica nanospheres

A Ce-CuZn catalyst with abundant Cu/Zn-OV-Ce active sites for CO2 hydrogenation to methanol

Pd/ZnO catalysts for direct CO2 hydrogenation to methanol

Tuning the product selectivity of CO2/H2O co-electrolysis by CeO2-modified proton-conducting electrolysis cells

Promoting CO Electroreduction to C2+ Oxygenates by Distribution of Water Dissociation Sites