Abstract:Polypeptides synthesized from alpha-amino acid N-carboxyanhydrides are considered ideal candidates as scaffold materials for bone tissue engineering due to their excellent biocompatibility and non-toxic degradation products. However, undesirable mechanical properties and osteoinductivity restrict their application in bone healing and regeneration. To overcome these limitations, we modified a synthetic polypeptide poly(N-epsilon-Cbz-(L)-lysine) (PZL) with poly(lactic-co-glycolic acid) (PLGA) having relatively high strength and osteoinductive bioglass (BG) particles, and fabricated foamy PZL/PLGA/BG composite scaffolds using a negative NaCl-templating method. The morphology, compression modulus, thermal and degradation behaviors of the PZL/PLGA/BG composite scaffolds were characterized, and the in vitro biocompatibility was evaluated with MC3T3-E1 cells using live/dead staining, MTT and ALP assays. The results indicated that the PZL/PLGA/BG composite scaffold with a weight ratio of 5 : 5 : 1 (PZL5PLGA5BG) had higher compression modulus and protein adsorption and mineralization abilities than other scaffolds, and was more conducive to the adhesion, proliferation and osteoblastic differentiation of MC3T3-E1 cells. The in vivo biocompatibility of the scaffolds was evaluated in both rat subcutaneous model and rabbit tibia defect model. The results of histological studies of subcutaneous implants, as confirmed by H&E, Masson's trichrome and CD34 staining assays, demonstrated that the PZL5PLGA5BG composite scaffolds allowed the ingrowth of tissue and microvessels and exhibited reduced inflammation response as compared to other scaffolds after 8 weeks of implantation. In experimental studies in bone defect model, the results of digital radiography and H&E staining confirmed that the PZL5PLGA5BG composite scaffolds after 8 weeks of implantation significantly improved in vivo osteogenesis. The newly formed bone tissue grew into the scaffolds along with the degradation of the materials. To sum up, the foamy PZL/PLGA/BG composite scaffolds had good comprehensive performances and would meet the needs of bone regeneration.

In Vitro Study of the PLLA-Mg65Zn30Ca5 Composites As Potential Biodegradable Materials for Bone Implants

Biodegradable Implant of Magnesium/polylactic Acid Composite with Enhanced Antibacterial and Anti-Inflammatory Properties.

In Vitro and Vivo Biocompatibility and Degradability of Low-Alloyed Mg-Zn-Ca-MgO Composite As Bone Repair Biomaterials

Microstructure, Mechanical Properties, In Vitro Biodegradability, and Biocompatibility of Mg-Zn/HA Composites for Biomedical Implant Applications

Study of Engineered Low-Modulus Mg/PLLA Composites As Potential Orthopaedic Implants: an in Vitro and in Vivo Study.

Regulating Degradation Behavior by Incorporating Mesoporous Silica for Mg Bone Implants.

Physicochemical properties and biocompatibility of PZL/PLGA/bioglass composite scaffolds for bone tissue engineering

Mg alloy rod reinforced biodegradable poly-lactic acid composite for load bearing bone replacement

Biocompatibility of magnesium-zinc alloy in biodegradable orthopedic implants

Nmgo-Incorporated PLLA Bone Scaffolds: Enhanced Crystallinity and Neutralized Acidic Products

Fabrication, Crystalline Behavior, Mechanical Property and In-Vivo Degradation of Poly(l–lactide) (PLLA)–Magnesium Oxide Whiskers (MgO) Nano Composites Prepared by In-Situ Polymerization

A comparative study on the in vivo degradation of poly(L-lactide) based composite implants for bone fracture fixation

Fully Degradable PLA-based Composite Reinforced with 2D-Braided Mg Wires for Orthopedic Implants

Microstructure, Mechanical Properties, in Vitro Degradation and Cytotoxicity of Mg-4zn-3ha Alloy for Biodegradable Implant Materials

A study on the in vitro and in vivo degradation behaviour and biocompatibility of a Mg-Mn-Zn alloy with PLLA and Micro arc oxidation composite coating

Study on the angiogenesis ability of Polymethyl methacrylate-mineralized collagen/Mg-Ca composite material in vitro and the bone formation effect in vivo

Mechanical properties and biomedical application characteristics of degradable polylactic acid–Mg–Ca3(PO4)2 three-phase composite

The microstructure, mechanical properties, corrosion performance and biocompatibility of hydroxyapatite reinforced ZK61 magnesium-matrix biological composite

In Vitro and in Vivo Studies on As-Extruded Mg- 5.25Wt.%zn-0.6Wt.%ca Alloy As Biodegradable Metal

In Vitro and in Vivo Investigation on Biodegradable Mg-Li-Ca Alloys for Bone Implant Application

In vivo biodegradation and biological properties of a Mg-Zn-Ca amorphous alloy for bone defect repair