Abstract:Natural rubber (NR) was self‐reinforced by mixing partially vulcanized NR (PNR) and then further normally vulcanization together. The PNR could be in situ fiberized and co‐vulcanized with the NR matrix and form a network with well‐bonded interface. As a result, the self‐reinforced NR (SNR) composites have excellent tear strength and other good mechanical performance including high elongation at break due to high elasticity of the PNR after complete vulcanization. In the contemporary modern mining sector, rubber conveyor belts are extensively and frequently utilized. Exceptional tear resistance and high elongation of the top cover rubber of the belt are imperative. In this investigation, a portion of natural rubber (NR) underwent partial vulcanization in advance. Subsequently, this pre‐vulcanized NR (PNR) was mixed with the NR matrix via mechanical blending. Due to the increased viscosity resulting from pre‐vulcanization, the PNR may disperse in the NR matrix, maintaining a specific microstructure without complete dissolution. During subsequent vulcanization, the PNR could co‐vulcanize with the NR matrix, forming a well‐bonded interface and ultimately yielding self‐reinforced NR (SNR) composites. The influences of the mass ratio of PNR to the NR matrix, sulfur content in PNR and pre‐vulcanization time on the mechanical properties of the SNR composites were thoroughly investigated. The results indicated that adding PNR effectively improved the tear strength of NR. When the PNR replaced 20 wt% of NR, sulfur content in PNR was 2.4 phr and pre‐vulcanization time was 2 min, the tear strength, stress at 300% elongation and wear resistance of SNR composites increased by 34.1%, 16.6%, and 10.2% compared to NR control sample, while elongation at break remained at 898%. These findings suggest that it is possible to enhance the tear strength of rubber without compromising elongation at break.

Study on Rubber Surface Enhancement of Fiber Fabric

A Facile Way to Modify Polyester Fabric to Enhance the Adhesion Behavior to Rubber

Influence of Surface Modification on the Tribological Properties of Hybrid Kevlar/PTFE Fabric Self-Lubricating Composites with Sodium Naphthalene Complex Solution

Enhanced Mechanical Properties of Natural Rubber by Block Copolymer-Based Porous Carbon Fibers

Microwave Irradiated Polyester Staple Fibers for Natural Rubber with Excellent Interface Performance

Wear Property Improvement by Short Carbon Fiber As Enhancer for Rubber Compound

Durability improvement of poroelastic road surface with treated rubber: Molecular dynamics simulation and experimental observations

Interface construction and properties of polyester fibers reinforced acrylonitrile-butadiene rubber coordination composites

STUDY OF IN-SITU MICRO-FIBRE OF EPDM/PA

Microstructure observation and viscoelastic relationship of surface modified rubber composites

Improvement of interfacial strength and fatigue stability of aramid fiber/rubber composites by constructing multiscale interphase structures

A dopamine-like deposition coatings on the polyethylene terephthalate fibers and its interface adhesion with rubber

Combined effect of interfacial modification and α-ZrP reinforcement on the tribological properties of PPS fabric/phenolic composites

Experimental Studies on Fatigue Damage of Polyester Reinforced Rubber

Self‐reinforced natural rubber composites: Preparation and properties study

Study of nylon textile-reinforced natural rubber composite

Surface Modified Alpha Zirconium Phosphate (Α-Zrp) Reinforced Natural Rubber Composites for Tire Tread Application

Improved Adhesion of Rubber Composites by Developing Environmentally Friendly Fiber Impregnation Coatings with Good Interfacial Modulus Transition Gradients

Enhanced fatigue resistance of plasma modified pyrolysis carbon black filled natural rubber composites

Mechanism on surface hydrophobically modification of fibrous wollastonite and its reinforcement of natural rubber

Study of Styrene Butadiene Rubber Reinforced by Polybutadiene Liquid Rubber-Modified Silica