Abstract:The natural pore structure of corn stalk core potentially contributes as a basic material for activated carbon. The activated carbon from a combination of chemical and physical activation is presented for capacitive energy storage. The chemical activation was carried out using 0.4 M KOH followed by pyrolysis process up to 600°C in an N2 atmosphere. The physical activation was conducted at various temperatures such as 600°C, 700°C, and 800°C with a CO2 gas flow rate of 10 mL/min. Supercapacitor cells were made from carbon electrodes of corn stalk core, 316L stainless steel as the current collector, duck eggshell as the separator, and 1 M H2SO4 as the electrolyte solution. The physical properties of carbon electrodes were characterized by identifying the density, surface morphology and chemical structure of carbon. The density value was obtained based on the mass, thickness, and diameter of the carbon electrode. The lowest density was found at the activation temperature of 700°C which has the potential to produce the best performance in supercapacitor cells. SEM was used to characterize the surface morphology. The activation temperature of 700°C showed the formation of irregular structures and provided large pores for the diffusion of electrolyte ions into the carbon matrix. The FTIR characterization was used to determine the carbon chain elements which formed double layers in supercapacitor cells. The electrochemical properties of supercapacitor cells were tested using cyclic voltammetry. Specific capacitances at the activation temperature of 600°C, 700°C, and 800°C were 90 Fg-1, 108.92 Fg-1, and 44.875 Fg-1, respectively. These results showed that the activation temperature of 700°C was the best temperature in the preparation of supercapacitor electrodes from corn stalk core as the biomass material.

CO2 Activation Temperature of Carbon Aerogel and Its Effects on Electrochemical Supercapacitor Performance

Preparation and Electrochemical Properties of PF-based Activated Carbon

Control of Nano Grains and Wide Carbocyclic Layer Space of Forming Active Carbon with Extraordinary Capacitance Characteristics in Supercapacitors

KOH Activation of Diatomite-templated Carbon and Its Electrochemical Property in Supercapacitor

Influence of KHCO3 Activation on Characteristics of Biomass-Derived Carbons for Supercapacitor

PREPARATION AND ELECTROCHEMISTRY PROPERTIES OF ACTIVATED CARBON ELECTRODE FOR SUPERCAPACITOR

Influence of Activated Condition on the Structure of Diatomite-templated Carbons and Their Electrochemical Properties As Supercapacitors

Activator concentration regulating the porous structure of activated carbon for supercapacitor application

Crucial structural parameters affecting electrochemical properties of activated electrospun carbon fibers as solid-state supercapacitor electrodes

The Effect of Activation Methods on the Electrochemical Performance of Ordered Mesoporous Carbon for Supercapacitor Applications

Carbon cryogel from resorcinol formaldehyde: tuning of processing steps and activation for use in supercapacitor

Influence of KOH Activation on Active Carbon for Supercapacitors

Pore Structure Regulation and Electrochemical Performance Characterization of Activated Carbon for Supercapacitors

Preparation and Electrochemical Properties of Multiscale Porous Active Carbon for Supercapacitor Electrodes Made from Ultra-Pure Lignite by Microwave Irradiation

Studies on preparation and performances of carbon aerogel electrodes for the application of supercapacitor

Trial Producing the Supercapacitor with Activated Carbon Fiber Electrode

A Comprehensive Study on Koh Activation of Ordered Mesoporous Carbons and Their Supercapacitor Application

Enhancing the pore wettability of coal-based porous carbon as electrode materials for high performance supercapacitors

Structural changes and electrochemical properties of mesoporous activated carbon derived from Eucommia ulmoides wood tar by KOH activation for supercapacitor applications

Regulating porous structure of coal-derived carbon materials by a dual-activation for high performance supercapacitors

Carbon Electrodes from Corn Stalk Core for Supercapacitor Application