Microstructure and corrosion resistance of AlTiN, AlTiN-Cu and AlTiN/AlTiN-Cu coatings

CHEN Hao,CHEN Kanghua,XU Yinchao,WANG Yunzhi,ZHU Changjun,PAN Chenxi

DOI: https://doi.org/10.11817/j.issn.1672-7207.2018.02.008

2018-01-01

Abstract:AlTiN, AlTiN-Cu and AlTiN/ AlTiN-Cu coatings were produced by cathode arc evaporation deposition equipment on WC-6％ Co substrates. Surface and cross-sectional morphologies of coatings were observed by SEM. Phase structures of coatings were studied by XRD. The corrosion resistances of coatings were investigated using Tafel polarization curve and electrochemical impedance spectroscopy in 3.5％ NaCl solution. The results show that the amount of droplets on AlTiN coating surface increases with the increase of addition of Cu, but the grain size of it is refined, and the structure is more compacted, and the porosity decreases. Compared with cemented carbide substrate, the corrosion current densities (icor) of AlTiN, AlTiN-Cu and AlTiN/AlTiN-Cu coated cemented carbides reduce by 40％,80％ and 93％, respectively, and the charge transfer resistances(Rct) of AlTiN, AlTiN-Cu and AlTiN/AlTiN-Cu coated cemented carbides increase by 2.91,3.72 and 7.85 times, respectively. Obviously, corrosion resistances of coated cemented carbides are greatly improved. The corrosion resistant abilities of three kinds of coatings decreases from large to small in following order: AlTiN/AlTiN-Cu, AlTiN-Cu and AlTN.