Abstract:This paper reports the synthesis of semiconductor nanocrystals of PbS through a facile and inexpensive synthetic route between lead acetate [Pb(Ac)2·3H2O] and dithioglycol (HSCH2CH2SH) without any surfactant. The products were characterized by x-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), Raman spectroscopy, x-ray photelectron spectroscopy (XPS) and infrared (IR) spectroscopy. The size of cube-shaped PbS nanocrystals can be controlled by changing the relative amount of Pb(Ac)2·3H2O and dithioglycol. Smaller cube-shaped PbS nanocrystals were obtained at higher sulfur content in the reaction system. The nanometre-sized single crystals of PbS measure ~83 nm × 59 nm × 22 nm and 39 nm × 10 nm × 7 nm, for lead acetate:dithioglycol ratios of 1:0.375 (denoted as PbS-1) and 1:1.5 (denoted as PbS-2), respectively, when a mixture of NaOH solution of lead acetate and ethyl alcohol solution of dithioglycol is maintained at 220 °C for 4 h in a Teflon-lined autoclave. XRD patterns and HRTEM images confirm the crystalline structure of the PbS crystals. TEM helped to determine the dimension of the single crystals. Raman, XPS and IR helped to further demonstrate the purity of the as-synthesized samples. The optical absorption spectra of suspensions of the these crystals in glycol show shifts in absorption band edge for as-prepared sample PbS-1 from 246 to 271 nm and for PbS-2 from 246 to 275 nm, after four days of storage, respectively. The photoluminescence peaks from the two samples are located at 434 and 433 nm for photoexcitation radiation of 315–355 nm, thus exhibiting a Stokes shift compared with band edge energy. The principal contribution of this work is that the nanometre-size PbS single crystals are prepared without using a surfactant or templating agent. The formation of a five-membered ring via the chelation between the Pb2+ ion and dithioglycol is considered to be crucial in this mechanism.

Microwave Assisted Synthesis of PbS Nanopartides by One-step Reaction

Synthesis of nanocrystalline lead chalcogenides PbE (E = S, Se, or Te) from alkaline aqueous solutions

Synthesis of lead sulfide nanocrystals via microwave and sonochemical methods

Synthesis and evolution of PbS nanocrystals through a surfactant-assisted solvothermal route.

High Yield Synthesis of PbS Nanocubes Using One-Step Solid-State Reaction in the Presence of an Anionic Surfactant

A novel aqueous-phase route to prepare flower-shaped PbS micron crystals

A Novel and Simple One-Step Solid-State Reaction for the Synthesis of PbS Nanoparticles in the Presence of a Suitable Surfactant

Synthesis of HgS and PbS Nanocrystals in a Polyol Solvent by Microwave Heating

Ultrasound-assisted synthesis of PbS quantum dots stabilized by 1,2-benzenedimethanethiol and attachment to single-walled carbon nanotubes

Surface Synthesis of PbS Nanoparticles on Silica Spheres by a Sonochemical Approach

Shape controlled synthesis of PbS nanocrystals by a solvothermal–microemulsion approach

Growth and photoluminescence properties of PbS nanocubes

One-step synthesis and optical properties of PbS quantum dots

Synthesis of CdS nanoparticles in water/DMF medium: an investigation on the effect of time and microwave irradiation

A Novel Hydrothermal Synthesis of Single Crystalline Pbs Nanorods and Their Characterization

Synthesis and Electrogenerated Chemiluminescence of PbS Nanospheres.

Microwave Heating Synthesis of Hgs and Pbs Nanocrystals in Ethanol Solvent

Studies of synthesis and optical properties of ZnS nanocrystals

A Novel Sonochemical Method for the Preparation of Nanophasic Sulfides: Synthesis of HgS and PbS Nanoparticles

Microwave Synthesis Of Nanocrystalline Metal Sulfides In Formaldehyde Solution

High yield synthesis of matchstick-like PbS nanocrystals using mesoporous organosilica as template