Abstract:Abstract In the present study, CoFe 2 O 4 and CoFe 2-x Gd x O 4 nanoparticles were synthesized by the hydrothermal process. The CoFe 2 O 4 nanoparticles were synthesized at different temperatures (70 o C, 100 o C, 150 o C, and 200 o C), molar ratio of CoCl 2 / FeCl 3 ( 0 / 2 , 0 . 75 / 2, 1 / 2, 1 . 5/2, and 2 / 2). Gadolinium-doped cobalt ferrite (CoFe 2-x Gd x O 4 ) nanoparticles have also been synthesized with Gd/Fe molar ratios of 0.18 and 0.53. The XRD patterns indicate that cobalt ferrite and Gadolinium-doped cobalt ferrite nanoparticles have been successfully synthesized without impurities with a medium degree of crystallinity. The XRD patterns show that by increasing the synthesis temperature from 70 o C to 200 o C, the size of the nanoparticles decreased from 50.49nm to 32.45nm while the morphology of the nanoparticles also changed from a shapeless and agglomerated state to a spherical shape. The XPS curve illustrated several peaks corresponding to Fe +3 , Co +2 , and O 1s. The binding energies for Co and Fe were consistent with Fe 2p and Co 2p binding energies for cobalt ferrite nanoparticles. The magnetic saturation value (M s ) increased from 17.253 emu/g to 54.438 emu/g with a rise in the synthesis temperature. The effects of FeCl 3 / CoCl 2 molar ratio on the magnetic properties showed the highest value of M s (54.438 emu/g) and the coercivity (H C ) of 744.56 Oe for a 2/1 molar ratio. The addition of gadolinium to the composition resulted in a reducing of the magnetic properties of nanoparticles; accordingly, the amount of saturated magnetization was reduced to 22.469 emu/g. Another effect of gadolinium dopant in the composition was a change in nanoparticle morphology from spherical to rod shape. The final aim of this study was to investigate the possible utilization of CoFe 2 O 4 and CoFe 2-x Gd x O 4 nanoparticles in medical treatment in the near future.

Hydrothermal Synthesis and Properties of CoFe2O4 Magnetic Nanoparticles

CoFe_2O_4 Nanoparticles Synthesized by Hydro-Thermal Method and Its Magnetic Properties

Synthesis and Magnetic Properties of CoFe<sub>2</sub>O<sub>4</sub> Nano-Particles

Synthesis of CoFe 2 O 4 nanoparticles with tunable magnetism by the modified hydrothermal method

Synthesis of CoFe<sub>2</sub>O<sub>4</sub> nanoparticles with tunable magnetism by the modified hydrothermal method

HYDROTHERMAL SYNTHESIS AND MAGNETIC PROPERTIES OF CoFe2O4 NANO-POWDER

Synthesis and magnetic properties of CoFe2O4 nanoparticles by using PEG as surfactant additive

Magnetic Properties for the Single-Domain CoFe2O4 Nanoparticles Synthesized by the Hydrothermal Method

Studies on the magnetism of cobalt ferrite nanocrystals synthesized by hydrothermal method

Synthesis, Structure and Magnetic Properties of CoFe2O4 Ferrite Nanoparticles

Synthesis of CoFe2O4 Nanoparticles via Solution Method and Their Magnetic Properties

Synthesis Factors Dependence of Magnetic Properties of CoFe2O4 and CoFe2-xGdxO4 Semicrystalline Nanoparticles with desired Morphology through Hydrothermal Procedure

Synthesis and Magnetic Properties of Nearly Monodisperse CoFe2O4Nanoparticles Through a Simple Hydrothermal Condition.

Chemical synthesis and magnetic properties of monodisperse cobalt ferrite nanoparticles

Solvothermal Synthesis and Magnetic Property of Monodispersed Fe_3O_4 Nano-powders

Synthesis and Magnetic Properties of Cobalt Ferrite (CoFe2O4) Nanoparticles Prepared by Wet Chemical Route

One-step hydrothermal synthesis and characterization of high magnetization CoFe2O4/Co0.7Fe0.3 nanocomposite permanent magnets

Hydrothermal Synthesis of Magnetic Fe_3O_4 Hexagonal and Single Crystal Nanorods

Size-controlled synthesis and magnetic properties of NiFe2O4 hollow nanospheres via a gel-assistant hydrothermal route

Hydrothermal Synthesis and Magnetic Properties of Fe3O4 Octahedral Microcrystals

The Synthesis and Thermal Effect of CoFe2O4 Nanoparticles