Study of SodiumSulfide on Corrosion Behavior of Q235 Steel in Sodium Hydroxide Solution

Xiaqiong YANG,Chaoyi CHEN,Junqi LI,Cong ZHAO,Long LIU,Guoling WEI
DOI: https://doi.org/10.15958/j.cnki.gdxbzrb.2016.04.08
2016-01-01
Abstract:The corrosion behavior of 16 Q235 steel in sodium hydroxide solution with different S2- concentration was studied by salt spray corrosion and electrochemical corrosion test and analyzed by corrosion weight loss meth-od, SEM, EDS and EIS. The results show that corrosion behavior of Q235 steel is notably affected by the concen-tration changing of S2-. Macro-morphology and micro-morphology analysis demonstrated corrosion of sample get worse with the growth of S2- concentration. EDS analysis demonstrated corrosion products were consist of Fe, S and O predominantly, the content of Fe was high when S2-concentration was 4g/L as the extent of corrosion was lightly. The content of O escalated when S2-concentration was 4g/L as oxidation of Fe. The content of S markedly elevated while the content of O dropped as the vulcanization reaction of Fe being dominant. Weight loss increased form 2.8732 g/m2 to 3.4451g/m2 and corrosion current density increased from 0.931μA/cm2 to 5.092μA/cm2 when S2- concentration increased from 3g/L to 6g/L as the reaction of S2-and Fe. However, the weight loss and corrosion current density showed an opponent trend when the S2- concentration grow up to 7g/L. The reason is that a dense membrane of FeS covered the surface of sample with 7g/L S2-.
What problem does this paper attempt to address?