Microstructure and Wear Reduction Properties of Graphene Carbon Nanotubes Hybrid Reinforced Aluminum Bearing Materials

Dong-song YIN,Ke-ju CHEN,Liang SONG,Yan-qi WANG

DOI: https://doi.org/10.3969/j.issn.1008-1402.2019.05.026

2019-01-01

Abstract:Aluminum-based bearing alloy (component: Al-20Sn-1Cu-0. 5Mg) , the friction coeffi-cient is reduced, which is of great significance in the dry friction process. In this paper, copper-plated gra-phene and carbon nanotubes were prepared by electroless plating, and copper -plated graphene and carbon nanotube hybrid modified aluminum-based bearing materials were prepared by ball-milling dispersion and hot-press sintering; metallographic microscopy ( OM) and scanning electrons were used. The microstructure of the composite was observed by microscope ( SEM) . The phase of the composite was analyzed by X-ray diffractome-try ( XRD) . The friction coefficient was tested by friction test. The results show that graphene and carbon nanop-article can be obtained by high energy ball milling. The tube is dispersed in the aluminum-tin composite pow-der, and the graphene and carbon nanotube -reinforced aluminum -tin -based bearing materials can be ob-tained by a hot press sintering process. Under the condition of dry friction, with the increase of graphene con-tent, the friction coefficient of aluminum matrix composites decreased significantly, and the fluctuation range also decreased significantly. When the graphene content was 1. 0wt. % , the average friction coefficient of composites decreased to 0. 12.