Abstract:Abstract It is always a difficult task to study the dynamic fracture of prefabricated cracks under stress wave loading. To investigate loadings of stress waves on dynamic cracks, a crack propagation testing configuration consisting of a one-point bend specimen loaded in split Hopkinson pressure bar (SHPB) was used, which loaded an unconstrained polymethyl methacrylate (PMMA) plate (120 mm × 60 mm × 5 mm) on the edge opposite to the cracked edge. A modified simple pre-cracked specimen geometry under impact stress wave loading to generate pure mode I crack at crack initiation was demonstrated, which can avoid the superposition and interference of various waves to facilitate the research. The numerical simulation was performed firstly by ABAQUS to prove the existence of the mode I field at the crack tip leading to crack propagation and indicate the stress distribution and evolution in the specimen caused by the propagation of the impact stress wave, analyze the propagation characteristics of the wave. Then dynamic caustics method in conjunction with high-speed photography was utilized in SHPB impact experiment. The propagation of shock stress wave in the specimen and its interaction with the prefabricated crack and the stress concentration at the tip of the prefabricated crack were analyzed. The corresponding stress intensity factor history is precisely determined. Finally, it is concluded that the observed distortion phenomenon at the impact point belongs to a caustic behavior under compression load, which reflects the stress concentration at the impact point. And the mode I failure occurs along the pre-crack direction. Specifically, the pre-crack shows obvious pure mode I crack propagation characteristics under symmetrical reflected tensile wave, the stress at the crack tip changes from compressive stress to tensile stress. And crack propagates under tensile stress wave reflected from its two free boundaries without crack, while the compressive stress wave can not make crack initiate and has little influence on crack propagation. Which agree with the numerical prediction.

Connecting modes of two cracks under impact loads

Investigation of Mixed-Mode Crack Propagation Behaviour under Impact Loading

Study of the effect of lengths on the propagation mechanism of interconnected cracks under impact loads

Cracking Behavior and Acoustic Emission Characteristics of Rock Containing a Single Preexisting Flaw

A Numerical Study On The Crack Development Behavior Of Rock-Like Material Containing Two Intersecting Flaws

Numerical study on crack propagation under explosive loads

Effects of a Circular Hole on the Propagation Behavior of Double Running Cracks under Impact Loading

Cracking Behavior of Concrete/rock Bi-Material Specimens Containing a Parallel Flaw Pair under Compression

Effect of Holes on Dynamic Crack Propagation under Impact Loading

Investigation on Fracture Properties of Single-Flawed Tunnel Model under Medium-to-Low-Speed Impacts

Study of Mixed-Mode I/II Fractures Using Single Cleavage Semicircle Compression Specimens under Impacting Loads

Study the effect of circular hole on dynamic fracture properties of cracked PMMA specimen under impact loads

Investigation Of Mixed-Mode I/Ii Fracture Under Impact Loading Using Split-Hopkinson Pressure Bar

Crack arrest characteristics and dynamic fracture parameters of moving cracks encountering double holes under impact loads

Investigation of the mechanical behavior of rock-like material with two flaws subjected to biaxial compression

Dynamic propagation behaviors of pure mode I crack under stress wave loading by caustics

Simultaneously Measuring Initiation Toughness of Pure Mode I and Mode II Cracks Subjected to Impact Loads

Crack Propagation and Coalescence of Brittle Rock-Like Specimens with Pre-Existing Cracks in Compression

Crack initiation characteristics of brittle materials with I‐II mixed mode crack under uniaxial compression

Compound-mode crack propagation law of PMMA semicircular-arch roadway specimens under impact loading

Rock-Concrete Interfacial Crack Propagation under Mixed Mode I-II Fracture