Sliding Wear Behavior of a Lithium Disilicate Glass-ceramic for Dentistry

Xuesong WANG,Zhenzhen ZHANG,Xiaocheng LI,Shaofeng ZHANG,Lin HE

DOI: https://doi.org/10.16078/j.tribology.2017.02.010

2017-01-01

Tribology

Abstract:Sliding wear behavior of a lithium disilicate glass-ceramic for dentistry was investigated using a pin-on-disk wear tester under the lubricating condition with artificial saliva.It is found that severe running-in wear exhibited because,the wear rate in the running-in region was much higher than that in the steady wear region.Decreasing the initial surface roughness of the wear surface shortened the running-in period and reduced the corresponding wear rate.Although the lithium disilicate crystalline phase in the microstructure of the glass-ceramic has higher hardness than the glass matrix,the crystalline phase was prone to spall predominantly in the running-in process,resulting in remarkable change of the worn surface roughness.The phenomenon was correlated with the lower elastic strain to failure (H/E ratio) of lithium disilicate crystalline phase.