Effect of Composition and Macropore Percentage on Mechanical and Biological Properties of 3D Precision Biomimetic Fabrication HA/-TCP Scaffold in Vitro
Wang Yanen,Wang Kai,Li Xinpei,Yang Mingming,Wei Qinghua,Chai Weihong
DOI: https://doi.org/10.3389/conf.fbioe.2016.01.01282
IF: 5.7
2016-01-01
Frontiers in Bioengineering and Biotechnology
Abstract:Event Abstract Back to Event Effect of composition and macropore percentage on mechanical and biological properties of 3D precision biomimetic fabrication HA/β-TCP scaffold in vitro Yanen Wang1*, Kai Wang1*, Xinpei Li1*, Mingming Yang1, Qinghua Wei1* and Weihong Chai1 1 School of Mechanical Engineering, Northwestern Polytechnical University, Industry Engineering Department, China Introduction: Room temperature 3D printing of composite biphasic bioceramics scaffolds with well distribute spraying collagen has great promise for fabricating synthetic bone implants with enhanced performance over traditional techniques[1]. Many manufacture parameters, such as the binder solution properties, have yet to be optimized to ensure maximal biocompatibility and osteoconductivity with sufficient mechanical properties. This study compared the phosphoric acid-based binder solution and polyvinyl alcohol to maximize cytocompatibility and mechanical strength, with a supplementation of Tween 80 to improve printing. In order to further enhance the biocompatibility, the collagen solution was sprayed to fabricate collagen-calcium phosphate composites. Reducing the viscosity and surface tension of the collagen solution through a physiologic heat treatment and Tween 80, respectively, enabled reliable thermal inkjet printing of the collagen solutions. Spraying the collagen solution with 1-2 wt% on the surface of each bioceramics layer significantly improved maximum flexural strength and cell viability. Materials and Methods: Previous studies[2]-[4] have shown that composition and macropore percentage (Pmacro) are two critical factors that affect the mechanical and biological properties of the 3D printed HA/β-TCP scaffold as Fig.1 shown. Therefore, in this study, HA/β-TCP scaffolds with six compositions ratios (HA wt% of 0%, 20%, 40%, 60%, 80% and 100%) and three Pmacro (0%, 30% and 50%) of polyvinyl alcohol and phosphoric acid HA/β-TCP scaffolds were fabricated using low temperature by three dimensional printing technology. Cell proliferation was continuously monitored using Cell Counting Kit-8 (CCK-8, MP biomedicals, USA). 1 × 105 cells/well were seeded onto each scaffold and cultured with regular α-MEM medium in 24-well plates. On D1, D4 and D7 the culture medium was changed to fresh α-MEM medium with 10% CCK-8 solution. The absorbance was measured at 450 nm using a microplate reader Power Wave XS (Bio-Tek, USA). Results and Discussion: The characteristics, total porosity (Ptotal), CS value and degradation of the printed scaffolds were measured. Properties of the prepared scaffolds have been studied though compressive strength experiment, porosity measurement, micro morphology observation, hydrophily. Compared with the polyvinyl alcohol scaffolds, the phosphate acid scaffolds have better mechanical properties. When the ratios of HA/β-TCP was wt 40% and 60%，the compressive strength and the tangent modulus were 4.8±0.23 Mpa and 200±29 Mpa, respectively. What is more, for the phosphoric acid scaffold, the porosity and macropore size of the printed specimens presented a variation of less than 5% compared to the scaffolds design. The phosphoric acid scaffolds (H40, HA wt% of 40%) showed remarkable ALP activity. To assess the bone healing performance, we have evaluated the in vitro biocompatibility of HA/β-TCP scaffolds by co-culturing with rabbit bone marrow-derived stem cells (BMSCs). The implants (Fig.2.) were confirmed to be osteoconductive, with new bone growth incorporating the degrading scaffold materials. Conclusion: this study demonstrates optimization of material parameters for 3D printed calcium phosphate scaffolds and enhancement of material properties by volumetric collagen incorporation via inkjet printing. The in vitro degradation of HA/β-TCP scaffolds was significantly affected by both the composition and the Pmacro, which showed an interactive effect (Fig. 3D, F=366.448, P=0.000). For scaffolds of a given Pmacro, the degradation decreased in the following order: pure β-TCP > BCPs > pure HA. The degradation decreased as the HA wt% increased. For scaffolds of a given HA wt%, the degradation among scaffolds with different Pmacro had significant differences (P＜0.05). The higher the Pmacro was, the higher the degradation was. Finally, the phosphoric acid scaffolds with HA wt% of 40% and Pmacro of 50% had no significant difference with the control group for cell proliferation. National Natural Science Foundation of China (51175432); National Natural Science Foundation of China (50905147); Doctor Special Science and Technological Funding of the China Ministry of Education (20116102110046); Fundamental Research Funds for the Central Universities (3102014JCS05007); the Key Industrial Science and Technology Projects of Shaan Xi Provience (No.2015GY047)References:[1] Bose, S.; Roy, M.; Bandyopadhyay, A., Recent advances in bone tissue engineering scaffolds. Trends Biotechnol 2012, 30, 546-554.[2] Schumacher, M.; Deisinger, U.; Detsch, R.; Ziegler, G., Indirect rapid prototyping of biphasic calcium phosphate scaffolds as bone substitutes: influence of phase composition, macroporosity and pore geometry on mechanical properties. Journal of Materials Science: Materials in Medicine 2010, 21, 3119-3127.[3] Gamblin, A. L.; Brennan, M. A.; Renaud, A.; Yagita, H.; Lezot, F.; Heymann, D.; Trichet, V.; Layrolle, P., Bone tissue formation with human mesenchymal stem cells and biphasic calcium phosphate ceramics: the local implication of osteoclasts and macrophages. Biomaterials 2014, 35, 9660-9667.[4] Detsch, R.; Schaefer, S.; Deisinger, U.; Ziegler, G.; Seitz, H.; Leukers, B., In vitro-osteoclastic activity studies on surfaces of 3D printed calcium phosphate scaffolds. J Biomater Appl 2010. Keywords: Cell Proliferation, in vitro, Bioprinting, 3D scaffold Conference: 10th World Biomaterials Congress, Montréal, Canada, 17 May - 22 May, 2016. Presentation Type: Poster Topic: Modeling cellular events in tissue regeneration Citation: Wang Y, Wang K, Li X, Yang M, Wei Q and Chai W (2016). Effect of composition and macropore percentage on mechanical and biological properties of 3D precision biomimetic fabrication HA/β-TCP scaffold in vitro. Front. Bioeng. Biotechnol. Conference Abstract: 10th World Biomaterials Congress. doi: 10.3389/conf.FBIOE.2016.01.01282 Copyright: The abstracts in this collection have not been subject to any Frontiers peer review or checks, and are not endorsed by Frontiers. They are made available through the Frontiers publishing platform as a service to conference organizers and presenters. The copyright in the individual abstracts is owned by the author of each abstract or his/her employer unless otherwise stated. Each abstract, as well as the collection of abstracts, are published under a Creative Commons CC-BY 4.0 (attribution) licence (https://creativecommons.org/licenses/by/4.0/) and may thus be reproduced, translated, adapted and be the subject of derivative works provided the authors and Frontiers are attributed. For Frontiers’ terms and conditions please see https://www.frontiersin.org/legal/terms-and-conditions. Received: 27 Mar 2016; Published Online: 30 Mar 2016. * Correspondence: Dr. Yanen Wang, School of Mechanical Engineering, Northwestern Polytechnical University, Industry Engineering Department, Xi'an, China, Email1 Dr. Kai Wang, School of Mechanical Engineering, Northwestern Polytechnical University, Industry Engineering Department, Xi'an, China, 1195665982@qq.com Dr. Xinpei Li, School of Mechanical Engineering, Northwestern Polytechnical University, Industry Engineering Department, Xi'an, China, 892431954@qq.com Dr. Qinghua Wei, School of Mechanical Engineering, Northwestern Polytechnical University, Industry Engineering Department, Xi'an, China, 598820042@qq.com Login Required This action requires you to be registered with Frontiers and logged in. To register or login click here. Abstract Info Abstract The Authors in Frontiers Yanen Wang Kai Wang Xinpei Li Mingming Yang Qinghua Wei Weihong Chai Google Yanen Wang Kai Wang Xinpei Li Mingming Yang Qinghua Wei Weihong Chai Google Scholar Yanen Wang Kai Wang Xinpei Li Mingming Yang Qinghua Wei Weihong Chai PubMed Yanen Wang Kai Wang Xinpei Li Mingming Yang Qinghua Wei Weihong Chai Related Article in Frontiers Google Scholar PubMed Abstract Close Back to top Javascript is disabled. Please enable Javascript in your browser settings in order to see all the content on this page.