Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

A Low-Cycle Fatigue Life Model for Simplified Turbine Disk Simulation Specimens of Powder Metallurgy Superalloys

A Modified Coffin-Manson Model for Ultra-Low Cycle Fatigue Fracture of Structural Steels Considering the Effect of Stress Triaxiality

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Effect of Initial Overload on the Low Cycle Fatigue Life of Gh4169 Alloy at Different Temperatures

Calculation of Finite Element of Thermal Stress and Analysis of Low-cyclic Fatigue Life for Non-central Hole Rotor of 135 MW Turbine

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

Characterization of Low Cycle Fatigue Performance of New Ferritic P92 Steel at High Temperature: Effect of Strain Amplitude

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

A New Empirical Life Prediction Model For 9-12%Cr Steels Under Low Cycle Fatigue And Creep Fatigue Interaction Loadings

Strain‐Controlled Low‐Cycle Fatigue Behavior of a Superalloy Considering Extensive Temperature Range and Stress Concentration

A novel LCF lifetime model for PM superalloys considering crack energy differences induced by surface underconstraint

An Approach to Estimate the Low Cycle Fatigue Probabilistic Curves of PBF-LB/M 316L Steel from Small Size Datasets Using the Remora Optimization Algorithm

Combined high and low cycle fatigue analysis of FGH96 alloy under high temperature conditions

LCF life prediction of turbine disc alloy using crystal plasticity and 3D representative volume element containing twin boundaries

A Low Cycle Fatigue Life Prediction Model Of Single Crystal Nickel-Based Superalloys Using Critical Plane Approach Combined With Crystallographic Slip Theory

New ultra-low cycle fatigue model for metal alloys

A Modified Normal Strain Ratio Fatigue Life Model Based on the Hybrid Approach of Critical Plane and Crystallographic Slip Theory

Microstructure evolution, failure mechanism and life prediction of additively manufactured Inconel 625 superalloy with comparable low cycle fatigue performance

Development of improved Manson-Coffin model considering the effect of yield stress under asymmetrical cyclic loading

Numerical Simulation of Low Cycle Fatigue Behavior of Ti2AlNb Alloy Subcomponents

Determination of relationship between high-temperature low cycle fatigue damage and mechanical property degradation: Experimental and theoretical analyses