Effect of Steady Torsion on Mode Ⅰ Fatigue Crack Growth in Automobile Steel Sheet

Te CHEN,Feng-peng YANG,Tian LAN

DOI: https://doi.org/10.15959/j.cnki.0254-0053.2017.04.019

2017-01-01

Abstract:This paper focused on experimental research of the effect of steady torsion on mode Ⅰ fatigue crack growth in two kinds of automobile steel sheet,SAPH440 and DP780.The effects of different steady torsion values combined-with same cyclic tension loading were discussed.The experimental results showed that steady torsion significantly retarded mode Ⅰ fatigue crack growth rate in both types of steel sheet.It decreased with increased constant torque when the torque was smaller than the critical value at which crack growth rate was slowest;otherwise,the retarding influence started to weaken.Procedure of crack propagation in automobile steel sheet under mode Ⅰ fatigue loading with a steady torsion was divided into the initial low-rate section and the subsequent accelerating section since crack growth rate was very low initially but increased rapidly subsequently with increase of crack length.To describe the crack growth rate data of the subsequent accelerating section,an effective stress intensity factor range and the modified Paris law were proposed based on linear elastic fracture mechanics.