Abstract:Ultrafiltration hollow-fiber membranes were prepared from polyetherimide (PEI) with a wet spinning method. The effects of N,N-dimethylacetantide (DMAc) as a solvent additive in the internal coagulant and acetic acid as a non-solvent additive in the dope solution on the morphologies and performances of the membranes were investigated. The influences of PEI dope concentration on membrane morphologies and properties were also studied. Scanning electron microscopy (SEM) indicates that the addition of DMAc into the internal coagulant changes the inner fiber surface from a dense skin layer to a porous structure. However, the pure water flux of the membrane decreases with the increase of DMAc content. On the other hand, the addition of acetic acid into the casting solution promotes the spinodal demixing of the membratte-forming system and suppresses the macrovoid formation in the membrane. A nodular structure forms in the fiber skin layer. With increasing acetic acid content, the pure water flux of the membrane increases about 4-fold and the solute retention shows a slight decrease. The mechanical properties can also be improved slightly by this additive. The thermal resistance of the PEI ultrafiltration membranes prepared in this work was examined by hot water treatment at 80 degrees C. No change was observed in the permeation performance of the membranes, while the study of mechanical properties shows that the elongation-at-break of the membrane decreases slightly. PEI was sulfonated by chlorosulfonic acid (CSA) in 1,2-dichloroethane. With the increase of the molar ratio of CSA to PEI repeat unit and/or reaction time, the ion-exchange capacity (IEC) of the sulfonated polyetherimide (SPEI) increases accordingly. Water uptake test and contact angle measurements show that the hydrophillicity of the SPEI increases with the increase of the IEC. Polyetherimide/sulfonated polyetherintide (PEI/SPET) ultrafiltration hollow-fiber membranes were also prepared with a dry-wet phase inversion method and SPEI was used as a polymer additive. SEM study reveals that the addition of SPEI induces the formation of nodular structure and suppresses the formation of finger-like macrovoids. With the increase of air-gap distance, it was found that the number of micropores formed in the outer fiber surface and the pore size increased. On the other hand, the pure water flux of the membrane reaches a maximum and then decreases, while the solute retention decreases at first and then levels off at longer air-gap. Based on the filtration of bovine serum albuntin (BSA) solution, it was found that the use of SPEI in the blend membranes increased their hydrophilicity.

Effects of Bore Fluid Flow Rate on the Morphologies and Properties of PEI Hollow Fibre Membrane

Effect of Coagulation Bath Temperature on the Structure and Performance of Polyethersulfone Hollow Fiber Membranes by Dry/wet Process

Effects of Preparing Condition on PVDF Membrane Morphology

Effect Of Polyethersulfone On The Mechanical And Rheological Properties Of Polyetherimide-Modified Epoxy Systems

Preparation and Structural Control of Polyethylene Hollow Fiber Membranes

Preparation of High Density Polyethylene/polyethylene- Block -Poly(ethylene Glycol) Copolymer Blend Porous Membranes Via Thermally Induced Phase Separation Process and Their Properties

Preparation and Performance of Polyethersulfone Hollow-Fiber Membrane

Ultrafiltration Hollow Fiber Membranes from Poly(Ether Imide): Preparation, Morphologies and Properties

Morphology and mechanical properties of poly(ether-imide)-modified polycyanurates

Experimental And Numerical Analyses On The Poly(Lactide-Co-Glycolide) Hollow Fiber Membranes

Effect of PEG Additives on Properties and Morphologies of Polyetherimide Membranes Prepared by Phase Inversion

The Effects of PEI Hollow Fiber Substrate Characteristics on PDMS/PEI Hollow Fiber Membranes for CO2/N2 Separation

Preparation And Performance Of Ultrafiltration Membranes From Polyetherimide And Its Sulfonated Derivatives

Influence of Dope Viscosity on the Fabrication of Pvdf Hollow Fiber Membranes with Single Skin Layer

Effect of Bore Fluid Composition on Poly(lactic-Co-glycolic Acid) Hollow Fiber Membranes Fabricated by Dry-Jet Wet Spinning

Porous Morphology and Mechanical Properties of Poly(lactide-Co-glycolide) Hollow Fiber Membranes Governed by Ternary-Phase Inversion

The Effects of Spinning Temperature on Morphologies and Properties of Polyethersulfone Hollow Fiber Membranes

Formation kinetics and characterization of polyphthalazinone ether ketone hollow fiber ultrafiltration membranes

Influences of the Chain Structure of PE‐b‐PEG on the Properties of PE/PE‐b‐PEG Blend Membranes Prepared by TIPS

Ultrafiltration Hollow Fiber Membranes of Sulfonated Polyetherimide/polyetherimide Blends: Preparation, Morphologies and Anti-Fouling Properties

Engineered pinhole-stitching process of PEI-based hollow fiber membrane enables preferred performance toward light gas separation