Abstract:Cables that have been in service for over 20 years in Shanghai, a city with abundant surface water, failed more frequently and induced different cable accidents. This necessitates researches on the insulation aging state of cables working in special circumstances. We performed multi-parameter tests with samples from about 300 cable lines in Shanghai. The tests included water tree investigation, tensile test, dielectric spectroscopy test, thermogravimetric analysis (TGA), fourier transform infrared spectroscopy (FTIR), and electrical aging test. Then, we carried out regression analysis between every two test parameters. Moreover, through two-sample t-Test and analysis of variance (ANOVA) of each test parameter, we analyzed the influences of cable-laying method and sampling section on the degradation of cable insulation respectively. Furthermore, the test parameters which have strong correlation in the regression analysis or significant differences in the t-Test or ANOVA analysis were determined to be the ones identifying the XLPE cable insulation aging state. The thresholds for distinguishing insulation aging states had been also obtained with the aid of statistical analysis and fuzzy clustering. Based on the fuzzy inference, we established a cable insulation aging diagnosis model using the intensity transfer method. The results of regression analysis indicate that the degradation of cable insulation accelerates as the degree of in-service aging increases. This validates the rule that the increase of microscopic imperfections in solid material enhances the dielectric breakdown strength. The results of the two-sample t-Test and the ANOVA indicate that the direct-buried cables are more sensitive to insulation degradation than duct cables. This confirms that the tensile strength and breakdown strength are reliable functional parameters in cable insulation evaluations. A case study further indicates that the proposed diagnosis model based on the fuzzy inference can reflect the comprehensive aging state of cable insulation well, and that the cable service time has no correlation with the insulation aging state.

Aging Mechanism and Research Progress of Cable Insulation Materials

Investigation on Thermal Aging and Degradation of XLPE for High Voltage Cable Applications

Effect of Tensile Stress on Insulation Properties of 500 Kv EHVAC XLPE Cable under Multi-Field Ageing

Multiscale Analysis of the Aging Process of Cable Insulation

Research on the Carrier Characteristics of Power Cables Considering the Aging Status of Insulation and Semiconducting Layers

Thermal aging characteristics and mechanism of insulation layer and semi-conductive shielding layer of high voltage cable

Effect of Thermal Ageing on Insulation Properties of 500 Kv DC XLPE Submarine Cable Insulation

Aging and life control of cross-linked polyethylene for cable insulation material

Influence of Thermal Aging on Dielectric Properties of High Voltage Cable Insulation Layer

Research on the thermal aging life prediction of XLPE cable

Experimental Study on Rejuvenation of Aged Power Cables via Simulation Operation

Thermal aging property and breakdown property of submarine cable materials

Insulation aging diagnosis and defect location of crosslinked polyethylene cable in the distribution network based on radio frequency identification

Heat Aging Test Research of XLPE Cable Insulation Based on NMR

Real time nondestructive aging sensors for cables

Study on Diagnostic Method of Aging 10kv XLPE Cable

Influence of Thermal Aging on Space Charge Characteristics and Electrical Conduction Behavior of Cross-Linked Polyethylene Cable Insulation

Studies of the Polarization/depolarization Current Characteristics of XLPE Cable

Damage of Cable Insulation with Pinhole Defect under the Acidic and Alkaline Environment

The Lifetime Prediction and Insulation Failure Mechanism of XLPE for High-Voltage Cable

Insulation diagnosis of service aged XLPE power cables using statistical analysis and fuzzy inference