Abstract:A kind of hydrophobic silica with good dispersibility was prepared first. The silica and epoxy natural rubber (ENR) were blended in Haake internal mixer at high temperature in a powerful shear force filed, and so the grafted silica was made through in-situ grafting reaction between the hydroxyl groups of silica and the epoxy groups of ENR. The grafting processes were performed as follows: first, the silica should be dried about 24 h at 100 degrees C in an oven to remove the free water molecules that absorbed on the surface of silica. Secondly, the grafting reaction temperature was chosen at 170 degrees C that confirmed by the test result of a Monsanto MDR-2000 moving die rheometer, and the weight proportions between silica and ENR were chosen to be 1: 1, 2: 1 and 3: 1 separately in this study. Thirdly, ENR was mixed in HAAKE internal mixer about I min, then silica was added to react with the ENR for another 15 min before discharged, and the outputs named ENR-grafted silica were obtained as we wanted. In order to obtain an appropriate grafting condition, the effect of different weight proportions between silica and ENR on the stress-strain curves of natural rubber composites reinforced by the grafted silica was discussed. Through analyses of the reinforcement effect, the appropriate proportion between silica and ENR was chosen to be 3: 1. FTIR, TGA and TEM analysis results indicated that ENR was successfully grafted onto the silica surface. FTIR result of the grafted silica showed the new absorptions. The peaks at 2966,2929 and 2862 cm(-1) are assigned to CH stretching vibrations. The absorption band at 1660 cm(-1) is characteristic of C C stretching. The stretching vibration of epoxy groups that should be at 870 cm-' was missing, suggesting the epoxy groups were almost used up to react with silanol groups. A new shoulder peak appears at 3640 cm(-1), which is ascribed to - 011 stretching of C-OH which is the result of the reaction of silanol groups and ENR. TGA curves revealed ENR grafted silica showed a new step between 348 - 449 degrees C due to the decomposition of ENR, and the grafting rate reached 21.3 %. TEM images indicated the size of silica agglomerates became small obviously after modification because of the grafting layer preventing the silica particles from conglomerating. Then, compared with the silica without grafting, the properties of NR composites filled with grafted silica were investigated. The "Payne effect" results indicated that the grafted ENR molecules reduced the silica-silica interaction by enhancing the rubber-silica interaction, and so the grafted silica had better dispersibility in natural rubber ( NR) composites. Mechanical properties test of NR composites proved that the grafted silica could more effectively improve the reinforcement effect due to the strong interface combination between silica and ENR. DMA results showed that the temperature of glassy transition of ENR bound to the silica surface shifted to higher temperatures. Consequently, the composite contained the grafted silica had high strength and high hysteresis at the same time on the normal temperature. So the composites have potential application in the shocking absorber products, the tire of racing cars, and so on.

GRAFTING OF RUBBER CHAIN ONTO THE FIBER SURFACE

Studies on grafting kinetics of bulk copolymerization of styrene onto rubber(I) - Grafting behavior

KINETICS OF BULK GRAFT COPOLYMERIZATION OF STYRENE ONTO RUBBER

Nondestructive Grafting of ZnO on the Surface of Aramid Fibers Followed by Silane Grafting to Improve Its Interfacial Adhesion Property with Rubber

Effect of silane coupling agent grafted glycidyl methacrylate on hollow microsphere/natural rubber composites

Polymer Grafting Onto Carbon Black by Solid State Method

High Efficient Grafting Polymerization of Styrene on Surface of NBR Latex and Physical Properties of NBR/NBR-g-PSt Composite

PREPARATION AND CHARACTERIZATION OF THE NATURAL RUBBER COMPOSITES REINFORCED BY EPOXY NATURAL RUBBER GRAFTED SILICA WITH GOOD DISPERSIBILITY

An efficient method to prepare high grafting montmorillonite with silane coupling agent and its improvements for styrene butadiene rubber composites

In situ Grafting onto Silica Surface with Epoxidized Natural Rubber via Solid State Method

Surface Modification of Aramid Fibers by Catechol/Polyamine Codeposition Followed by Silane Grafting for Enhanced Interfacial Adhesion to Rubber Matrix

Effect of epoxy functionalized elastomer modified carbon fiber on mechanical properties and interfacial adhesion of chloroprene rubber (CR)/natural rubber (NR) composites

Physical Insight for Grafting Polymer Chains onto the Substrate via Computer Simulations: Kinetics and Property

Influence of Chain Lengths on Interfacial Performances of Carbon Fiber Reinforced Polyarylacetylene Resin Composites

Enhancing Performances of Polyamide 66 Short Fiber/Natural Rubber Composites via In Situ Vulcanization Reaction

Surface Modification of UHMWPE Fibers by Ozone Treatment and UV Grafting for Adhesion Improvement

Effect of Surface Activity of Carbon Black on the Strength of Filler Network and Filler-Rubber Interaction

A dopamine-like deposition coatings on the polyethylene terephthalate fibers and its interface adhesion with rubber

Study on the surface grafting of polypropylene fibers

Grafting of Active Carbon Nanotubes Onto Carbon Fiber Using One-Pot Aryl Diazonium Reaction for Superior Interfacial Strength in Silicone Resin Composites

Promoted Dispersion Of Silica And Interfacial Strength In Rubber/Silica Composites By Grafting With Oniums