Preparation,characterization and performance of hyperbranched polyester grafted carboxylated multi-walled carbon nanotubes

Qiao-qiang LV,Li-sha PAN,Nai XU,Su-juan PANG,Xue-qiong YIN,Long-min CHEN
DOI: https://doi.org/10.3969/j.issn.1004-1656.2018.04.017
2018-01-01
Abstract:Multi-walled carbon nanotubes were carboxylated with mixed acids whose volume ratio of sulfuric acid/nitric acid was 3: 1,and then the hyperbranched polyester was grafted to the surface of the carboxylated MWCNTs,which was the preparation of hy-perbranched polyester grafted carbon nanotubes.The products were characterized by XPS,TGA,Raman and tested for dispersibility in water and chloroform.The results showed that the O/C values of carbon nanotubes increased from 0.076 to 0.301 by carboxyla-tion.The loss weight of carboxylated carbon nanotubes and hyperbranched polyester grafted carbon nanotubes increased from 0.74%to 11.34%and 13.07%respectively.Raman spectra appeared blue shift phenomenon and ID/IGvalues also increased with carboxyl-ation and graft modification.Solubility test found that hyperbranched polyester grafted multi-walled carbon nanotubes significantly increased hydrophilicity.After 60 days,they could still be stably and evenly dispersed in water.Good hydrophilicity created the con-ditions for the application of carbon nanotubes in other fields.
What problem does this paper attempt to address?