Abstract:A core-shell hybrid nanostructure, possessing a hard backbone of multiwalled carbon nanotube (MWNT) and a soft shell of brushlike polystyrene (PS), was successfully prepared by in situ atom transfer radical polymerization (ATRP), using Cu(I)Br/N,N,N',N",N"-pentmethyldiethylenetriamine (PMDETA) as the catalyst, at 100 degreesC in diphenyl ether solution. The molecular weight of PS was well controlled, as was the thickness of the shell layer. TEM images of the samples provided direct evidence for the formation of a core-shell structure, i.e., the MWNT coated with polymer layer. FTIR, H-1 NMR, SEM, and TGA were used to determine the chemical structure, morphology, and the grafted PS quantities of the resulting products. To further establish the covalent linkage between PS and MWNT moieties, the resulting PS-functionalized MWNTs were defunctionalized by hydrolysis or by thermal decomposition. Comparative studies, based on TEM and SEM images between the PS-functionalized and chemically defunctionalized MWNT samples, also revealed the covalent coating character. GPC analysis showed that the number-average molecular weight (M.) of the grafted PS chains ranged from 5000 to 11000 with a relatively broad polydispersity index (PDI, ca. 1.77-3.57). Further copolymerization of tert-butyl acrylate (tBA) with the PS-linked MWNTs as initiators was realized, illustrating that (1) the PS species is still "living" although the lower controllability of PDI and (2) acrylate-type monomers can be copolymerized with styrene-type ones on the sidewalls of the MWNT. We believe that achieving these hybrid objectives, on the basis of such simple grafting, will pave the way for the design, fabrication, optimization, and eventual application of more functional carbon nanotube-related nanomaterials.

The preparation of highly water-soluble multi-walled carbon nanotubes by irreversible noncovalent functionalization with a pyrene-carrying polymer.

Preparation of water-soluble multi-walled carbon nanotubes by polymer dispersant assisted exfoliation.

A Simple Polymerizable Polysoap Greatly Enhances the Grafting Efficiency of the “Grafting-To” Functionalization of Multiwalled Carbon Nanotubes

SOLUBILITY IMPROVEMENT AND SURFACE FUNCTIONALIZATION OF MULTI-WALLED CARBON NANOTUBES BY A THIOL-FUNCTIONALIZED POLY(PHENYLACETYLENE) DERIVATIVE

Functionalization of Carbon Nanotubes by Corona‐Discharge Induced Graft Polymerization for the Reinforcement of Epoxy Nanocomposites

Solvent-dependent Fluorescence Property of Multi-Walled Carbon Nanotubes Noncovalently Functionalized by Pyrene-Derivatized Polymer

Water soluble multi-walled carbon nanotubes prepared via nitroxide-mediated radical polymerization

Preparation of Water-Soluble Multi-Walled Carbon Nanotubes by Ce(IV)-induced Redox Radical Polymerization

Hydrothermal treatment to prepare hydroxyl group modified multi-walled carbon nanotubes

Functionalization of Multiwalled Carbon Nanotubes with Polystyrene under Atom Transfer Radical Polymerization Conditions

Functionalization of Multiwalled Carbon Nanotubes by Atom Transfer Radical Polymerization and Defunctionalization of the Products

Preparation and Properties of Functionalized Carbon Nanotube/psf Blend Ultrafiltration Membranes

A New Approach to Functionalize Multi-Walled Carbon Nanotubes by the Use of Functional Polymers

Surface Functionalization of Single-Walled Carbon Nanotubes Using Photolysis for Enhanced Dispersion in an Organic Solvent

Enhanced Dispersion of Nanotubes in Organic Solvents by Donor-Acceptor Interaction Between Functionalized Poly(Phenylacetylene) Chains and Carbon Nanotube Walls

Polyurea-Functionalized Multiwalled Carbon Nanotubes

Coating carbon nanotubes with polymer in supercritical carbon dioxide.

Synthesis of Water-Soluble Multiwalled Carbon Nanotubes with Grafted Temperature-Responsive Shells by Surface RAFT Polymerization

Functionalization of multi-walled carbon nanotubes with non-reactive polymers through an ozone-mediated process for the preparation of a wide range of high performance polymer/carbon nanotube composites

Improved dispersibility of multi‐wall carbon nanotubes with reversible addition–fragmentation chain transfer polymer modification

Functionalization Of Multi-Walled Carbon Nanotubes By Thermo-Grafting With Alpha-Methylstyrene-Containing Copolymers