Novel temperature responsive P(MEO2 MA-co-OEGMA-co-HMAM) self cross-linked hydrogel

Wei-juan SHENG,Shou-xin LIU,Qin-qin WANG,Xuan LI,Na-er GUANG

DOI: https://doi.org/10.3969/j.issn.1004-1656.2015.09.016

2015-01-01

Abstract:A novel temperature responsive copolymer,poly(2-(2-methoxyethoxy)ethyl methacrylate-co-oligo(ethylene glycol)meth-acrylate-co-N-hydroxymethylacrylamide) [ P ( MEO2 MA-co-OEGMA-co-HMAM ) ] , was synthesized by atom transfer radical poly-merization(ATRP). The copolymer was characterized by FTIR,1H NMR,and gel permeation chromatography(GPC). Temperature sensitivity for the copolymer and the effects of salts on the lower critical solution temperature( LCST) of copolymer aqueous solutions were studied by transmittance measurements at different temperatures. Then,the hydroxyl groups on P(MEO2MA-co-OEGMA-co-HMAM) chains were transformed into azide or alkyne groups respectively. A temperature-sensitivity self-cross linking hydrogel was prepared by click chemistry among the copolymers P(MEO2MA-co-OEGMA-co-HMAM). Rheological kinetics of gel formation dem-onstrated that gelation had commenced within 1 minutes,and since then the storage modulus( G′) was higher than the loss modulus (G″). The pore size and swelling ratio of the prepared hydrogels decreased with increasing the temperature because hydrophobic polymer-polymer interactions results in the self-aggregation of PMOH chains at a higher temperature ( T>LCST ) , that proved the formed hydrogel had temperature sensitivities. BSA and anethole respectively were used as a model hydrophilic and hydrophobic drug to examine in vitro the sustained release from hydrogel. Results showed that the anethole release rate from hydrogel within 10 h at 37℃ was slower than BSA.