NOVEL Ph AND TEMPERATURE-SENSITIVE HYDROGELS

LM Tang,Y Dai

DOI: https://doi.org/10.3321/j.issn:1000-3304.2003.03.019

2003-01-01

Abstract:New pH and temperature-sensitive hydrogels have been synthesized through copolymerization of anionic acrylate polyurethane prepolymer (P(U)) and N-isopropyl acrylamide (NiPAAm) under various feed ratios. Single glass transition temperature was noticed from the DSC curves of the dried hydrogels, indicating of good miscibility between the two components. The pH sensitivity was much affected by the composition of the hydrogels and a lowest swelling degree was shown in hydrogel H4 with P(U)/NIPAAm feed ratio of 1/1.Hydrogel H4 also possessed lower critical solution temperature (LCST) of about 27degreesC at both pH = 11 and pH = 7 solutions. In the equilibrium hydrogel most of the absorbed. water was freezable water with its content little affected by the hydrogel. composition Furthermore,the gel strength was improved with incorporating more P(U) chains into the hydrogel.