Synthesis and Electrochemical Properties of Li[Mn1/3-x/3 Ni1/3-x/3 Co1/3-x/3 Crx ]O2 As Cathode Materials for Lithium-ion Secondary Batteries

LIN Xao-jing,LI Shu-hua,HE Ze-zhen,LIU Xing-quan

DOI: https://doi.org/10.3969/j.issn.1005-1511.2005.05.004

2005-01-01

Abstract:The layered Li[Mn_(1/3-x/3)Ni_(1/3-x/3)Co_(1/3-x/3)Cr_x]O_2(x=0,0.015,0.025,0.050,0.100) materials were prepared by means of an improved solid-state reaction,and their physical and electrochemical properties were investigated by XRD,SEM and electrochemical testing techniques.When(x=)0 and 0.015,the mean size of samples is about 800 nm and the samples have uniform morphology and normal grain-size distribution.The materials showed only one plateau between 2.5 V～4.5 V.A significant structure transformation to the spinel-type phase was not found in the charge-discharge cycling.The layered structure was stabilized and the discharge capacity was also increased by doping appropriate amount of Cr~(3~+).The 1.5 mol% chromium-doped active materials exhibited the best cycle performance.It delivered an initial discharge capacity of 138.60 mAh· g~(-1) in a cut-off range between 2.5 V and 4.5 V at room temperature,but the capacity and retention were found to decrease when the concentration of Cr~(3~+) was over 1.5 mol%.