Achieving High-Strength, High-Porosity and Relatively Low-Shrinkage in Extrusion-Based 3D Printed ZrO2 Ceramics by Adjusting CaCO3 Addition and Sintering Temperature
Yuxiao Lin,Fuchu Liu,Liang Zhang,Yi Wang,Miao Wang,Yanzhao Li,Ming Wu,Zheng Li,Hao Liu,Guangchao Han
DOI: https://doi.org/10.1016/j.jallcom.2024.176809
IF: 6.2
2024-01-01
Journal of Alloys and Compounds
Abstract:High-strength, high-porosity and relatively low-shrinkage ZrO2 ceramics were successfully fabricated by material extrusion 3D printing technology via optimizing CaCO3 addition and sintering temperature. The effects of different CaCO3 additions on the performance, phase formation, and microstructure of porous ZrO2 ceramics sintered at different temperatures were systematically investigated and discussed. The results showed that flexural strength, porosity and shrinkage of the ZrO2 ceramics were significantly affected by CaCO3 addition and sintering temperature. The appropriate addition of CaCO3 could promote sintering and phase transformation of m-ZrO2, increase the number and size of pores in the matrix. The corresponding flexural strength and porosity of the sintered samples increased, while the shrinkage rate decreased. The raised sintering temperature appropriately facilitated the formation of CaZrO3. Microstructural analysis indicated that CaZrO3 exhibited a larger polyhedral bulk morphology, mainly distributed at the edges of pores, which could stabilize the pore structure and thicken the sintering necks, and thereby exhibiting well-balanced comprehensive performance. The ZrO2 ceramics with high flexural strength, high porosity and relatively low shrinkage rate were achieved by adding 15 wt% CaCO3 and sintering at 1450 degree celsius. The resulting flexural strength and porosity were 27.33 MPa and 67.62 %, respectively, presenting an improvement of 563.35 % and 13.69 % compared to ZrO2 ceramics without CaCO3. Moreover, the shrinkage rates in the X-direction (9.98 %), Y-direction (9.62 %), and Z-direction (9.94 %) significantly reduced, decreasing by 38.28 %, 38.10 %, and 41.46 %, respectively.