EXPERIMENTAL STUDIES ON AN IN SITU SETTING POROUS CARBONATED HYDROXYAPATITE CEMENT AS A NEW INJECTABLE BONE SUBSTITUTE

唐佩福,王继芳,卢世璧,王岩,卢世琳,贺大为,郝立波,毛克亚,黄晋香,孙明学,汪爱媛,赵彬

2005-01-01

Abstract:Objective To prepare a new injectable carbonated hydroxyapatite cement(CHC) which can set in situ and has porous configuration.Methods To prepare an in situ setting porous CHC(PCHC),the 0.35% P-chitosan(PC) were added to make injectable PCHC(IPCHC).And the biocompatibility,PH value,time of solidify,mechanical property,chemical component,molecular structure,porous configuration,injectability and anti-washout ability were tested.Results 0.35% PC as a adjuvant was added to pore agent to prepare IPCHC.The porosity character and its injectability can be controlled by adjustment of the component.The test results demonstrate that the self-setting composition of this cement is carbonated hydroxyapatite,which is similar with natural cancellous bone.The porosity is 37.2% with interconnect pores;the setting time is 12 to 16 minutes,which is suitable for surgical application;the compressive strength is 4.3±2.6 Mpa,which is equal to that of cancellous bone;the cytotoxicity tests show an excellent biocompatibility;the concentration of CO32-is 5.6%,which is close to that of natural bone hydroxyapatite;the injection index of IPCHC is 95.13%±1.11%,which is significantly higher than that of PCHC(68.78%±2.19%);and IPCHC has good anti-washout ability.Conclusion Adding 0.35% PC to the liquid phase of the cement can improve its injectability greatly,and obtain a good anti-washout result.The IPCHC is useful to reconstruct non-loading bone defects in miniinvasive surgery,especially for the blooding site.