Abstract:This study was carried out to evaluate the effect of acid etching versus laser etching of dentin surface on the bonding of Composite and Compomer restorative materials to dentin surface by studying microleakage at the dentin-filling interface, compositional analysis of dentin surface, and Scanning Electron Microscopic (SEM) study of the bonding area. 120 freshly extracted premolar teeth were divided according to surface treatment into three groups. Group I (Acid etching group) contained thirty teeth. Twenty teeth were selected to assess microleakage by forming standardized class V cavity on the buccal surface of the selected teeth. Then, teeth were subdivided into two subgroups with 10 teeth in each. Subgroup (i) delivered composite filling while subgroup (ii) delivered compomer filling according to manufacturer instructions. microleakage at the dentin-filling interface of teeth was examined using dye penetration method. dye penetration scores at occlusal and gingival margins were recorded and tabulated. Five dentin surfaces of five teeth from group I were etched by acid then prepared for compositional analysis of dentin surface by Infra-Red (IR) Spectroscopy. Another Five dentin surfaces were etched by acid then prepared for (SEM) assessment. Group II (Laser etching group) contained ninety teeth, twenty teeth were used for assessing microleakage after laser etching taking similar steps to that of acid etching. Thirty dentin surfaces of thirty teeth were etched by laser with different parameters then prepared for compositional analysis of dentin surface by IR Spectroscopy. Thirty dentin surfaces of thirty teeth were etched by laser with different parameters then prepared for SEM assessment. Group III (Untreated group) contained ten teeth that were left untreated. Five dentin surfaces of five teeth were subjected to IR Spectroscopy assessment. Five dentin surfaces of five teeth were prepared for SEM assessment. The results revealed that acid etching of dentin surface resulted in significant less leakage compared to laser etching. IR Spectroscopy revealed changes in dentin surface structure indicating that there was a reaction occurred by the acid and laser etching. SEM assessment showed more openings of dentinal tubules in case of acid etching, while in case of laser etching, there were a surface structural changes with a melting and fusion dentin surface. Acid etching of dentin gives better results on the bonding of Composite and Compomer filling materials than laser etching and thus gives more successful clinical condition. Further investigations are needed by using different types of laser to get more benefit from applications of laser clinically.

Scanning Electron Microscopic Observation of Human Dentine of Permanent and Primary Teeth after Chemo Mechanical Removal of Dental Caries Tissue

The influence of caries-affected dentin on bonding effect of deciduous teeth

Evaluation of dentin features in teeth after caries removal by three techniques (chemomechanical, mechanical with a smart bur, and air-abrasion): an in vitro study

Effect of Carisolv chemo-mechanical caries removal on microtensile bond strength

An in-vitro evaluation of residual dentin retained after using novel enzymatic-based chemomechanical caries removal agents

Clinical evaluation of caries removal with a chemo-mechanical Carisolv method

An in vitro assessment of the residual dentin after using three minimally invasive caries removal techniques

SEM Evaluation of Tooth Surface after a Composite Filling Removal Using Er:YAG Laser, Drills with and without Curettes, and Optional EDTA or NaOCl Conditioning

Microhardness and characterization of human dental tissue after application of enzymatic chemical agents: In vitro study

Scanning electron microscopic observation of primary tooth dentin following final irrigation with 95% ethanol: An in vitro study

Comparative study of the effect of laser irradiation and acid etching surface treatment on bonding of some dental restorative materials To dentin surface

Root Canal Wall Dentin Structure in Uninstrumented but Cleaned Human Premolars: A Scanning Electron Microscopic Study

A Scanning Electron Microscope Evaluation of the Efficacy of Different Fluoride-releasing Dental Restorative Materials to Prevent Enamel Demineralization: An In Vitro Study

Effects of Tetracycline, EDTA and Citric Acid Application on Nonfluorosed and Fluorosed Dentin: An In Vitro Study

A Comparative Evaluation of the Effects of Three Remineralizing Agents on Bleached Enamel: A Scanning Electron Microscopy (SEM) Analysis

Scanning Electron Microscopic Observation of Inhibitory Effect of Chelerythrine on the Adherence of Streptococcus Mutans

Study on the normal and pathologic structures of the hard dental tissues using the scanning electron microscope.

Cytotoxicity and dentin composition alterations promoted by different chemomechanical caries removal agents: A preliminary in vitro study

[Scanning Electron Microscopy Was Used to Observe Dentin Morphology in Primary and Permanent Teeth Treated by Erbium: Yttrium-Aluminum-garnet Laser].

The effect of final irrigation with different solutions on smear layer removal and dentin erosion: A scanning electron microscope study

Scanning electron microscopy evaluation of smear layer removal using ethylenediaminetetraacetic acid, etidronic acid, and chitosan nanoparticle solution as root canal irrigants