Abstract:STATEMENT OF PROBLEM: Yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) ceramic material has been reported to possess exceptionally high flexural strength; however, the strength of Y-TZP ceramics can be affected by surface treatments performed by dental laboratory technicians and by intraoral conditions.PURPOSE: This study investigated the influence of low-temperature-degradation (LTD) treatment, airborne-particle abrasion, and polishing on the flexural strength and structural stability of a Y-TZP ceramic material.MATERIAL AND METHODS: By sectioning zirconia ceramic blocks (Vita In-Ceram YZ blocks) into 25 x 4 x 2-mm bars, 310 specimens were fabricated and divided into 9 groups: Group C, as-sintered (control); group B24h, boiled in water for 24 hours; group B7d, boiled in water for 7 days; group H6h, stored in humidified air at 250 degrees C for 6 hours; group H24h, stored in humidified air at 250 degrees C for 24 hours; group H7d, stored in humidified air at 250 degrees C for 7 days; group P, polished; group A, airborne-particle abraded; and group AB, airborne-particle abraded and boiled for 7 days. The flexural strengths (MPa) of all specimens were determined by using a 3-point bending test. The variability was analyzed by using Weibull statistics. Pairwise differences among the 9 groups were evaluated by using confidence intervals (95%) for scale and shape parameters. From every block used, 8 specimens were obtained and every specimen was marked according to the location of its origin from the original block. Surfaces of the specimens were evaluated by using scanning electron microscopy (SEM) at various magnifications. X-ray diffraction analysis was performed to identify possible tetragonal-to-monoclinic phase transformations. Energy dispersive spectroscopy (EDS) was used to obtain information on the chemical composition.RESULTS: Aging or "finishing" treatments had no significant negative effects on flexural strengths. Mean flexural strengths ranged from 796.7 to 950.2 MPa. Group A exhibited the highest mean flexural strength (950.2 MPa). Weibull modulus values ranged between 5.6 and 9.3. Tetragonal-to-monoclinic phase transformation was detected for a specimen boiled for 24 hours. More tetragonal-to-monoclinic phase transformation was detected for specimens boiled for 7 days and stored in humidified air at 250 degrees C for 7 days. The SEM examination of fractured surfaces revealed sintering defects, and EDS analysis showed less yttria concentration on Y-TZP specimens that were boiled for 7 days.CONCLUSION: Within the limitations of this study, the results suggested that the LTD procedures and the polishing treatment used did not reduce the flexural strengths of zirconia bars. Airborne-particle abrasion increased the flexural strength of specimens.CLINICAL IMPLICATIONS: Although polishing, airborne-particle abrasion, and various low-temperature degradation (LTD) treatments did not significantly degrade the strength of the Y-TZP ceramic material, LTD resulted in loss of yttria. Over time, gradual dissolution of yttria could decrease the tetragonal-phase stability and long-term clinical serviceability of this dental ceramic material.

The research of influencing factors of low-temperature degradation on dental zirconia

[Study on Low Temperature Degradation of Dental Zirconia Ceramic].

Low temperature degradation of Y-TZP ceramic for dental applications

[Research progress on the low-temperature degradation of zirconia in prosthetic dentistry].

The research of aging time and thickness on the low-temperature degradation of dental zirconia

Effect of Aging Time and Thickness on Low-Temperature Degradation of Dental Zirconia.

Effects of Low Temperature Degradation on Zirconia Ceramic(px-242A)

Development and Characterization of Al2O3/SrAl12O19 Reinforced Zirconia with High Fracture Toughness and Low-Temperature Degradation-Resistant for Dental Applications

Effects of Low-Temperature Aging on Mechanical Properties of Two Kinds of Dental Zirconia Ceramics

Effect of low-temperature degradation on the fatigue performance of dental strength-gradient multilayered zirconia restorations

The effect of surface treatment and low-temperature degradation on flexural strength of additive manufactured zirconia

Terahertz Probing of Low‐temperature Degradation in Zirconia Bioceramics

Comparison of the Low Temperature Degradation Properties of Two Y-TZP Ceramics for Dental Applications

Intraoral low-temperature degradation of monolithic zirconia dental prostheses: Results of a prospective clinical study with ex vivo monitoring

Research on the Low-Temperature Degradation of Dental Zirconia Ceramics Fabricated by Stereolithography.

Evaluation of Feasibility on Dental Zirconia-Accelerated Aging Test by Chemical Immersion Method

Microstructure and Nanoindentation Analyses of Low-Temperature Aging on the Zirconia-Porcelain Interface.

Intraoral low-temperature degradation of monolithic zirconia dental prostheses: 5-year results of a prospective clinical study with ex vivo monitoring

Hydrothermal Ageing and Its Effect on Fracture Load of Zirconia Dental Implants

Dielectric probing of low-temperature degradation resistance of commercial zirconia bio-ceramics

In vitro evaluation of low-temperature aging effects and finishing procedures on the flexural strength and structural stability of Y-TZP dental ceramics