Abstract:Objectives: This study aims to investigate bond strength between zirconia and resin cement through surface treatments with Er: YAG laser, Nd: YAG laser, and Si-Zr coating. Methods: Seventy-five round pre-sintered zirconia discs with a diameter of 18 mm and a thickness of 1.5 mm were prepared by a powder compactor. Fifty discs were randomly divided into five groups of 10 discs each and were subjected to five surface treatments: no treatment (control group), sandblasting with alumina particles (sandblasting group), Er: YAG laser treatment (Er: YAG laser group), Nd:YAG laser treatment (Nd: YAG laser group), and Si-Zr coating treatment (Si-Zr coating group). The discs were then bonded to composite resin columns with resin cement. The shear bond strength of each group was tested with a universal tester. Roughness tester, scanning electron microscope (SEM), and energy dispersive spectroscopy were used to analyze surface performance. Results: The bond strength of the Si-Zr coating group was higher than that of the remaining groups (P<0.05). The difference in bond strength between the sandblasting group and the Er: YAG laser group was not statistically significant (P>0.05), but both of them had higher bond strength than the Nd: YAG laser group (P<0.05). The Si-Zr coating group had the highest surface roughness (P<0.05). The surface roughness of the sandblasting, Er: YAG laser, and Nd: YAG laser groups was higher than that of the control group (P<0.05), but the difference among the three groups was not statistically significant (P>0.05). SEM observations showed irregular scratches on the surface of the sandblasting group and large pits with holes on the surface of the Er: YAG and Nd: YAG laser groups. In the Er: YAG laser group, the crystal structure was replaced by a smooth surface with a large amount of microcracks due to partial melting. Complex porous structures that comprised "island-like" structures and mass pores among the grains were observed on the surface of the Si-Zr coating. Only Zr, O, and Y were detected on the surfaces of the control, Er: YAG laser, and Nd: YAG laser groups. Al was found on the surface of the sandblasted group, and a higher proportion of Si was detected on the surface of the Si-Zr coating group. Conclusions: Er: YAG laser and Nd: YAG laser treatment on the zirconia ceramic surface could increase roughness and improve the bond strength to resin cement. Si-Zr coating treatment is an effective alternative for increasing the roughness and bond strength of zirconia surface and is superior to sandblasting and laser treatments.

Effect of cold plasma treatment on the zirconia-resin cement bond strength

[Effects of Different Surface Treatments on the Zirconia-Resin Cement Bond Strength].

Effects of Cold Atmospheric Plasma Treatment on Resin Bonding to Hightranslucency Zirconia Ceramics

Effect of Different Cleaning Methods on Bond Strength and Surface Wettability of High Translucency Zirconia

Effect of Er: YAG laser and plasma treatment on the bond strength of Y-TZP

Effects of Sandblasting on Surface Character and Resin Bond of Zirconia Ceramic

Effects of different plasma treatments on bonding properties of zirconia

The effects of four primers and two cement types on the bonding strength of zirconia

Effect of Surface Treatment with Zirconium Dioxide Slurry on the Bond Strength of Resin Cement to Ultratranslucent Zirconia

Effect of laser and coating surface treatment on the bond strength of zirconia ceramics

In vitro short-term bonding performance of zirconia treated with hot acid etching and primer conditioning

[Effect of a Chemical Primer on the Bond Strength of a Zirconia Ceramic with Self-Adhesive Resin Cement].

Influence of Hot-Etching Surface Treatment on Zirconia/Resin Shear Bond Strength

Oxygen Plasma Improved Shear Strength of Bonding Between Zirconia and Composite Resin

A new surface treatment method: fusing glass ceramic to zirconia

Influence of Cold Atmospheric Plasma on Surface Characteristics and Bond Strength of a Resin Nanoceramic.

The Shear Bond Strength of Resin-Based Luting Cement to Zirconia Ceramics after Different Surface Treatments

[Effect of Surface Treating Methods on the Shear Strength of Luting Cements to Cercon Zirconia].

Effect of Hot-Etching Treatment Duration on the Shear Bond Strength of Zirconia-to-resin Cement.

Improving the bonding stability between resin cements and zirconia-based ceramic using different surface treatments

Investigating the impact of different cleaning techniques on bond strength between resin cement and zirconia and the resulting physical and chemical surface alterations