Abstract:Purpose: To evaluate the shear bond strength (SBS) of resin composite to dentin contaminated with artificial saliva (AS) containing mucin and amylase using an experimental method controlling the volume of saliva and adhesive in a defined surface area. Methods: Flat bonding surfaces were prepared on extracted human molars (320 grit surface). Using adhesive tape, a 4.5 mm bonding window was prepared on the dentin surfaces. Groups (n= 12) were prepared using the etch & rinse (ER) or self-etch (SE) modes for Adhese Universal (ADH), Scotchbond Universal Plus (SBU), and Prime & Bond active (PBA) dental adhesives (DA). For the control (C) groups, the adhesives were applied per the manufacturers' instructions with 2.0 µl or 3.0 µl of the adhesive. For the saliva-contaminated groups, 1.0 µl of artificial saliva with mucin was applied in the bonding window either dried or allowed to remain wet before the application of either 2.0 µl or 3.0 µl of the adhesive. After the adhesive film was air dried and light cured using an Ultradent bonding fixture, Spectrum TPH3 was bonded to the prepared surfaces. After water storage for 24 hours at 37°C, the specimens were debonded and shear bond strength (SBS) was calculated (MPa). A Kruskal-Wallis test with Bonferroni correction was used to determine group differences (P< 0.05). Scanning electron microscopy (SEM) was performed to visualize the interfacial surfaces prepared using an ion-etching technique. Results: Mean SBS for the three adhesives were similar in both ER and SE modes to uncontaminated dentin surfaces for all the control groups. For dentin contaminated with dried or wet saliva, both the surface condition and the adhesive system were significant factors at a confidence level of 95%. For the dried saliva test groups, ADH and PBA with 3.0 µl of adhesive generated similar SBS values to controls while SBU generated lower values. Lower values were generated when using 2.0 µl of adhesive for the three adhesives in SE and ER modes except for PBA in the ER mode. Using wet saliva and 3.0 µl of adhesive ADH and SBU generated lower SBS values while PBA generated similar values to controls. Under SEM, morphology at the adhesive dentin interfaces was similar among the adhesives to uncontaminated dentin but notable differences were observed for SBU and ADH for both wet and dried saliva-contaminated surfaces. Clinical significance: Salivary contamination differentially affects shear bond strength and the morphology of the bonded interface of universal adhesives to dentin. These differences are specific to the adhesive tested and are influenced by using the etch and rinse or self-etch strategies and the volume of adhesive used. When concerned about salivary contamination clinically, maximizing the volume of adhesive on the substrate may help mitigate the deleterious effects of saliva contamination.

The effects of the compatibility between resins and different adhesives on the shear bond strength and micro-leakage

Bonding Effectiveness of the Universal Adhesive on Caries-Affected Dentin of Deciduous Teeth

Effects of matching adhesives and composite resins on microleakage

Bond Strength, Microleakage, Microgaps, and Marginal Adaptation of Self-adhesive Resin Composites to Tooth Substrates with and without Preconditioning with Universal Adhesives

A Research on Bond Strength and Interface of Dentin Adhesives

Shear bond strength of universal adhesives to human enamel and dentin

Comparative evaluation of bonding performance between universal and self-etch adhesives: In vitro study

Micro-shear bond strength of resin composite cement to coronal enamel/dentin, cervical enamel, cementoenamel junction and root cementum with different adhesive systems

Bond Strength of Two Resin Cements with Leucite-reinforced Ceramic Using Different Bonding Agents

[Effects of Three Self-Etch Adhesives and Mild Salivary Contamination on the Bonding Durability of Deciduous Teeth].

Microleakage of three dentin adhesive systems in Class V restorations

Cross-compatibility of methacrylate-based resin composites and etch-and-rinse one-bottle adhesives

Comparative Evaluation of Shear Bond Strength and Microleakage of Two Self-adhering Composite Resins: An in vitro Study

Bonding Quality of Etch-and-Rinse Adhesives in Root Canals Upon Different Pretreatments.

[Influence of Different Resin Bond Systems on Coronal Microleakage of Fiber Posts and Core Restorations].

SEALING OF BONDED RESIN COMPOSITE TO GINGIVAL WALL FOLLOWING APPLICATION OF TWO HEMOSTATIC AGENTS USING TWO ADHESIVE PROTOCOLS: AN INVITRO STUDY

Effect of Chemical Removal or Mechanical Modification of Smear Layer on Dentin Adhesion with Universal Resin Adhesives

BONDING ABILITY OF DIFFERENT LINERS TO BULK-FILL RESIN COMPOSITE USING SILANE-CONTAINING ADHESIVE

Effects of Saliva Contamination on Bonding Performance of Self-Etching Adhesives

Marginal integrity of low-shrinkage and methacrylate-based composite resins: Effect of three different hemostatic agents

Effects of salivary contamination on the shear bond strengths of universal adhesives to dentin