Abstract:Objectives: This study aimed to assess the surface roughness, surface free energy (SFE), and shear bond strength (SBS) on a lithium disilicate glass-ceramic surface following varying etching protocols (time variation) and application of silane either with or without adhesive material. Methods and materials: Lithium disilicate glassceramic (LDGC) computer-aided design and computer-aided manufacture (CAD/CAM) blocks were cut using a slow-speed cutting mechanism. CAD/CAM blocks were then evaluated for surface roughness, 6 groups (n=20); SFE,12 groups (n=5); and SBS, 10 groups (n=10). The cut CAD/CAM blocks were randomly allocated to 28 groups. Groups were based on the following: 30 or 90 seconds of etching with 9% hydrofluoric acid (HF); application or absence of silane coupling agent (Sil); and application or absence of adhesive (Adh).The control group (Cont) had untreated surfaces. Unetched surfaces were surveyed with only silane (Sil), only adhesive (Adh), or silane+adhesive (SilAdh). Further etched groups were HF30 with HF for 30 seconds, HF30-Sil, HF30-Adh, and HF30-SilAdh. Alternative 90-second etching times produced similar groups: HF90, HF90-Sil, HF90-Adh, and HF90-SilAdh. A digital profilometer was used to assess the surface roughness of specimens, and two readings were recorded. Sessile drop analysis was used to examine SFE specimens, and the OWRK model was modified to measure liquid surface tension. A universal testing machine (UltraTester, Ultradent Products, Inc, South Jordan, UT, USA) was utilized for the SBS test, with the crosshead speed set at 0.5 mm/min until failure. Representative treated specimens from each group were submitted to surface morphological evaluation and chemical analysis using scanning electron microscopy/energy dispersive x-ray spectroscopy (SEM/EDXS) (n=3). After data collection, evaluation using one- or two-way analysis of variance and the post-hoc Tukey test (α=5%) was conducted. Results: A longer etching time of 90 seconds produced a rougher surface. After the 90-second etching process, SFE displayed the greatest values; nevertheless, the use of silane did not affect SFE. For every group examined, the application of silane followed by adhesive resulted in an increase in SBS and more stable bonding over time. SEM/EDXS showed that etching times did affect the amount of cerium on the surface and altered surface morphology. Conclusions: Higher and more consistent bond strengths have been observed with longer etching periods. Silane and adhesive application on the ceramic surface showed stronger and enhanced bond strength, specifically when longer etching times were employed.

The Effect of Hydrofluoric and Silane Coupling Agent on the Bonding Strength Between IPS E.max Press Ceramic and Resin Cement

Effect of different etching conditions on the bonding strength between IPS e.max~ Press ceramic and resin cement

The Effect of Three Porcelain Etching Agents Combine with Silane Coupling Agent on the Bond Strength Between Cerinate Porcelain and Composite Resin

Effects of Different Silane Coupling Agents on Porcelain/Composite Resin Bonding Interface

The effect of long-chain silane coupling agent on the bond strength between ceramic and resin cement

The Effects of Different Silane Coupling Agents on Porcelain/Composite Resin Chemical Bonding

Effect of Etching Time and Resin Bond on the Flexural Strength of IPS E.max Press Glass Ceramic.

[Effect of Hydrofluoric Acid Etching Time and Resin Bonding on the Flexural Strength of Lithium Disilicate Glass Ceramic].

Effect of siloxane quantity and ph of silane coupling agents and contact angle of resin bonding agent on bond durability of resin cements to machinable ceramic.

Effect of Silane Coupling Agent on Composite-Composite Bond Strength: an in Vitro Study

Study on the resin-ceramic adhesive bond strength using silane coupling agent treated by hydrolysis catalysts

Chemical adhesion rather than mechanical retention enhances resin bond durability of a dental glass-ceramic with leucite crystallites

Effect of Different Etching Times with Hydrofluoric Acid on the Bond Strength of CAD/CAM Ceramic Material

Effect of Hydrofluoric Acid Etching Time on the Resin Bond Durability of Glass Ceramic

Effect of Silane Pretreatment on the Immediate Bonding of Universal Adhesives to Computer‐aided Design/computer‐aided Manufacturing Lithium Disilicate Glass Ceramics

Effect of Heated Silanization on the Bond Strength Between Ceramic and Resin Composite

Influence of etching time on the shear bond strength between IPS-Empress 2 ceramics and adhesive resin cement

Optimal Hydrofluoric Acid Etching Duration and Impact of Silane/Adhesive on Profilometric Properties and Bonding to Lithium Disilicate Glass Ceramics

The effect of adhesive surface with porcelain sintering and two silane coupling agents on the adhesive properties of zirconia

Increasing Acid Concentration, Time and Using a Two-Part Silane Potentiates Bond Strength of Lithium Disilicate–Reinforced Glass Ceramic to Resin Composite: An Exploratory Laboratory Study

Effects of hydrogen peroxide pretreatment and heat activation of silane on the shear bond strength of fiber-reinforced composite posts to resin cement