Release control of formaldehyde emission from veneered panels modified with nanoparticles

Zhao LI,Yu LIU,Xiaodong ZHU

DOI: https://doi.org/10.13360/j.issn.2096-1359.2017.06.004

2017-01-01

Abstract:It is well-known that formaldehyde is a kind of indoor air pollution source.As an biochemical degradation method,photocatalytic degradation is non-toxic,safe,high catalytic activity,and quick effect.Photocatalytic oxidation technology is an environmental friendly technology,dealing with the poisonous and difficult degradable organic pollutants.It has been widespread concerned in nanometer dtunium dioxide with high chemical stability.The advantages of good photocatalytic performance and low cost has made it become the most widely used as semiconductor photocatalytic materials recently.In this study,the effect of nano-materials on formaldehyde emissions from wood-based panels was investigated.The surface decoration materials,melamine-impregnated paper and wood veneers with different thicknesses,were impregnated with nano-modified melamine resin.Using the micro veneer and melamine-impregnated paper as the objects,the effects of three kinds of impregnated materials on the formaldehyde controlled release were explored when the nano titanium dioxide was doped in melamine resin.The results showed that the addition of nano titanium dioxide can significantly reduce the formaldehyde emission of wood-based panels.With the increase in nano titanium dioxide content,the formaldehyde emission of the wood-based panel decreased gradually.Among them,the formaldehyde emission released from the veneered panels was the lowest,which was only 32.9％ of untreated panels as the addition percent of nano titanium dioxide increased to 2％.The properties of the nano-modified melamine resin adhesive were characterized by the Fourier transform infrared spectroscopy (FT-IR) and differential scanning calorimetry (DSC).The results showed that no new compounds were formed during the mechanically mixture of nano titanium dioxide and melamine resin,and the curing of adhesive was not affected during the hot-pressing.But the wettability of the nano-modified decorative material was affected in some degree.