Effect of Degassing Time on Aggregation Structure and Chain Structure of XLPE Cable Insulation Material

Zhiwei LI,Haiyun JIN,Tao ZHANG,Shichao NIE,Jiangang ZHANG,Naikui GAO,Yili WANG
DOI: https://doi.org/10.7652/xjtuxb201804003
2018-01-01
Abstract:The crosslinked polyethylene (XLPE) is degassed in laboratory,and the crosslinking by-products content,the aggregation structure and the chain structure are investigated by tensile test,degree of crosslinking measurement,infrared spectroscopy,differential scanning calorimetry (DSC) and scanning electron microscopy (SEM) at different degassing time.The results show that the crosslinking by-products are effectively eliminated during the degassing process,and the acetophenone content is significantly reduced after 168 h degassing,then the reduction rate slows down and remains unchanged until 336 h.However,the reduction rate of cumyl alcohol content is small,the degassing trend slows down after 336 h.Experimental results show that the optimum degassing time of XLPE cable is limited within 168-336 h.In the beginning of degassing,the free radicals inside XLPE insulation are cross-linked again and the chain structure changes,which increases elongation at break.And there are two kinds of aggregation structure changes in crystal nucleus formation and crystalline grain growth.The newly developed small crystals facilitate further promoting elongation at break,the spherocrystal growth becomes perfect,and the crystallinity increases.Moreover,the duration of chain structure changes for a shorter period while the duration of aggregation structure changes for a longer period,and those changes remain stable in the late degassing.According to the above experimental results,a change model of aggregation and chain structure of XLPE cable insulation in the degassing process is constructed,and the changes of microstructure and macroscopic elongation at break are explained.
What problem does this paper attempt to address?