Abstract:Core-shell structured SiC/SiO2 nanowires (SiC/SiO2 NWs) were synthesized by a simple thermal evaporation method without a catalyst. The influence of the growth temperature and holding time on the microstructure and composition of the nanowires were investigated. The results indicate that within the temperature range of 1150 to 1550 degrees C, the color of SiC/SiO2 nanowires gradually transitions from pure white to off-white with increasing temperature. During this process, the average diameter of SiC/SiO2 increases from 74 nm to 291 nm, while the surface SiO2 layer thickness decreases from 17 nm to 5 nm, with nanowires can reach lengths of hundreds of micrometres. Variations in supersaturation of SiO and CO at different temperatures lead to discrepancies in nanowire diameter and SiO2 shell thickness. At 1350 degrees C, prolonged holding time enhances silicon powder reaction, resulting in increased structural disorder of the obtained SiC/SiO2 nanowires. The nanowire growth follows a vapor-solid (V-S) mechanism. Additionally, the study demonstrates that the photoluminescence (PL) characteristics of the nanowires exhibit a blue shift attributable to their nanoscale dimensions, while variations in emission spectra correlate with stacking faults, SiC diameter, and SiO2 thickness. This work may be provide a theoretical basis for preparing SiC/SiO2 nanowires with different diameters and SiO2 shell thicknesses, which is crucial for advancing the development and application of SiC/SiO2 nanoceramics.

Formation and Morphology Evolution of Nanowires on Biomorphic SiC Ceramics

Tuning the Morphologies of SiC Nanowires Via the Change of the CoxSiy Melts

Tuning the morphologies of SiC nanowires via the control of growth temperature, and their photoluminescence properties.

Growth and Morphology of One-Dimensional SiC Nanostructures Without Catalyst Assistant

Morphology of Silicon/Silicon-Oxide Nanowires Grown from Nickel-Coated Silicon Wafers

Morphological Evolution of One-Dimensional SiC Nanomaterials Controlled by Sol–gel Carbothermal Reduction

Microstructure Evolution and Growth Mechanism of Core-Shell Silicon-Based Nanowires by Thermal Evaporation of SiO

Synthesis and Microstructure of Epitaxial SiC Nanowires

Morphology Evolution of Si Nanowires Synthesized by Gas Condensation of SiO Without Any Catalyst

Surface-migration Driving Uniform Amorphous Shell on Crystalline Nanowire: the Case of SiC/SiOx Core–shell Nanowires

Observation of SiC Nanodots and Nanowires in Situ Growth in SiOC Ceramics

Formation Mechanism of Silicon Carbide Nanotubes with Special Morphology

Preparation and formation mechanism analysis of morph-genetic SiC fiber fabric ceramic

Microstructure And Properties Of Porous Sic Ceramics Modified By Cvi-Sic Nanowires

Growth of Multi-Morphology Amorphous Silicon Oxycarbide Nanowires During the Laser Ablation of Polymer-Derived Silicon Carbonitride

Microstructure analysis of morph-genetic SiC/C ceramics from wood

The Formation of Symmetric SiC Bi-Nanowires with a Y-shaped Junction.

In-situ Synthesis of SiC/SiO2 Nanowires by Catalyst-Free Thermal Evaporation of Silicon Powder and Their Photoluminescence Properties

Adjusting the Morphology and Properties of SiC Nanowires by Catalyst Control

SiO2 Nano-Crystals Embedded in Amorphous Silica Nanowires

Synthesis and Characterization of SiC Nanowires Using Silicon Evaporation