Abstract:The performance of the CFRP–steel interface is crucial to the reinforcement efficiency of the steel structures strengthened by using externally pasted CFRP sheet method; while it is influenced significantly by adhesive properties and geometrical characteristics of joints. The present study aims to optimize the adhesive layer of the CFRP–steel interface and establish a theoretical model of predicting the interfacial behaviors of the optimized CFRP–steel joints. A commercially available adhesive was modified by addition of Nano-SiO2 ranged from 0 to 7wt% to ascertain the optimal content of Nano-SiO2. A series of tensile tests were carried out on dog-bone adhesive specimens, single-lap shear specimens and CFRP–steel double-lap joints to obtain the mechanical properties of the adhesive at different content of nanofiller and the corresponding bond–slip laws in the unmodified and modified CFRP–steel interfaces. Accordingly, theoretical models were derived to predict the load capacity of the joints and the bond stress distribution along the CFRP–steel interface during different loading phases. The results show that the mechanical properties of the adhesive are improved with the addition of nano-SiO2 up to 1.4 wt%. When the content of nano-SiO2 rises from 1.4 to 7 wt%, the tensile and shear strengths as well as the tensile modulus decline gradually whereas the ductility keeps growing with a lower growth rate. These indicate the nano-SiO2 content of 1.4 wt% is favorable. Both the peak stress and the load capacity of the CFRP–steel joint increase with the adhesive thickness varying from 0.5 to 1 mm. The bond–slip law of the unmodified CFRP–steel interface can be simplified to be bilinear, regardless of the adhesive thickness and curing duration. In contrast, the modified interface presents a trilinear curve due to the special plastic plateau caused by the filling of nano-SiO2. Consequently, a larger fracture toughness and a higher load capacity can be reached by the optimized joints. The theoretical results are in agreement with the experimental phenomena and results. The modified adhesive is beneficial to utilize the CFRP material better and improve the reinforcement efficiency.

Effect of the adhesive type on the bond behavior of the CFRP plate-to-steel bonded interfaces

Experimental study on dynamic behavior of CFRP-to-steel interface

Experimental Study on Bond Behavior between CFRP Plates and Steel Substrates Using Digital Image Correlation

Experimental Study on the Bond Behavior Between CFRP Plates and Steel Substrates under Fatigue Loading

Experimental Study on the Bond Behavior of the CFRP-steel Interface under Rapid Loading

Effects of mechanical properties of adhesive and CFRP on the bond behavior in CFRP-strengthened steel structures

Experimental Study on the Bond Behavior of CFRP-steel Interfaces under Quasi-Static Cyclic Loading

Determination of the Bond–slip Behavior of CFRP-to-steel Bonded Interfaces Using Digital Image Correlation

An Experimental Study on Shear Performance of Adhesive Interface Between Steel Plates and CFRP

Experimental Behaviour Of Cfrp-To-Steel Bonded Interfaces

Experimental Study on Mixed Mode-I & II Bond Behavior of CFRP-to-steel Joints with a Ductile Adhesive

Bond-slip Models for CFRP Plates Externally Bonded to Steel Substrates

Effects of Adhesive Property and Thickness on the Bond Performance Between Carbon Fiber Reinforced Polymer Laminate and Steel

Bond-slip model of the CFRP-steel interface with the CFRP delamination failure

Numerical Modelling of Bond Behaviour Between Steel and CFRP Laminates with a Ductile Adhesive

Research On The Interfacial Bond Behavior Between Cfrp Sheet And Steel Plate Under The Static Load

Experimental and theoretical study on mechanical behaviors of CFRP–steel interface

Interfacial Bond-Slip Degradation Relationship Between CFRP Plate and Steel Plate under Freeze-Thaw Cycles

Study on the Interface Constitutive Relation between Carbon Fiber Fabric and Steel

Experimental Study on Debonding Failure of Steel Beams Strengthened with a CFRP Plate

Experimental Study on the Carbon-Fiber-reinforced Polymer–steel Interfaces Based on Carbon-Fiber-reinforced Polymer Delamination Failures and Hybrid Failures