Influence Of Doping Zr On The Performance Of Ceo2-Zro2-Al2o3 Composite Oxide After Reductive Heat Treatment

Yang Huang-Gen,Tan Yu-Fang,Wei Qing-Min,Yan Quan,Chen Yuan,Zhu Li-Gang,Qin Li-Qin,Xiao Yi-Hong
DOI: https://doi.org/10.11868/j.issn.1001-4381.2019.000455
2020-01-01
Journal of Materials Engineering
Abstract:Ceria-zirconia-alumina composite oxides CZ(x)A (the molar ratios of Ce, Zr and Al are 1 : x : 2, x=0, 0. 5, 1, 1. 5 and 2) fresh samples were prepared by the co -precipitation method. The samples were thermally aged in a flowing air atmosphere and in 10% H-2/Ar flow. The structure and performance of the composite oxides were studied by X-ray powder diffraction (XRD), N-2 adsorption desorption (BET), oxygen storage capacity MSC) measurements, and H-2 temperature-programmed reduction (H-2-TPR). The results show that for CZ(x)A samples, with the increase of the content of Zr, no CeAlO3 phase is observed in the CZ(1.5) A-H-2-1100 and CZ(2)A-H-2-1100 samples which are reductively aged at 1100 degrees C; the oxygen storage capacity ((CSC) is 713 mu mol . g(-1) and 548 mu mol . g(-1) respectively, far higher than the 23 mu mol . g(-1) of CZA-H-2-1100; and the hydrogen consumption of H-2-TPR is 1995 mu mol . g(-1) and 2087 mu mol . g(-1), respectively, while the hydrogen consumption of CZA-H-2-1100 was significantly reduced to 310 mu mol . g(-1). The OSC of ClzA is affected by the formation of CeAlO3 during the reductive treatment, which is consistent with the change result of the hydrogen consumption of H-2-TPR. It was found that CA samples are more likely to produce CeAlO3 after reductive treatment, and the CZ(1.5) A and CZ(2)A samples doped with a certain amount of Zr elements in CA can inhibit the formation of CeAlO3, thus significantly improve the oxygen storage performance and the hydrogen consumption of H-2-TPR of the material. Furthermore, CZ(x)A have better reduction performance at low temperature after reductive treatment.
What problem does this paper attempt to address?