Preparation of double-shell phase change and humidity storage micro-capsules with uniform particle size distribution

Hao ZHANG,Lei XIONG,Ziru XU,Xiuyu LIU

DOI: https://doi.org/10.13801/j.cnki.fhclxb.20170112.003

2017-01-01

Abstract:With n-octadecane,methyl methacrylate and chitosan as the core material,inner shell and outside shell respectively,the double-shell phase change and humidity storage micro-capsules were made by in-situ polymerization and emulsion interfacial polymerization method.Combining the uniform design and radial basis function neural net-work,the effect of parameters (i.e.emulsifier amount,co-emulsifier amount,initiator amount,phacoemulsification time and mixing speed)on particle size distribution of double-shell phase change and humidity storage micro-capsules were investigated.In addition,the optimal uniform particle size distribution of double-shell phase change and humid-ity storage micro-capsules were tested and characterized.The results show that radial basis function(RBF)neural network has the best approximation effect when "Spread"is 0.55 .To obtain optimal uniform particle size distribu-tion for double-shell phase change and humidity storage micro-capsules,the preparation parameters are identified as follows:emulsifier amount to be 3.58wt%,co-emulsifier amount to be 0.53wt%,initiator amount to be 1.86wt%, phacoemulsification time to be 11.35 min and mixing speed to be 632 r·min-1 .On the base of the above preparation parameters,d10 is 3352.0 nm,d50 is 4474.9 nm,d90 is 6108.4 nm,and the measured value of d90 -d10 is 2756.4 nm.Therefore,the measured value agrees well with the predictive value (relative error is 2.69%).In the case of relative humidity between 35% and 65%,the equilibrium moisture content is obtained to be between 0.0547 g·g-1 and 0.1259 g · g-1 , phase transition temperature is 28.87℃ and phase change enthalpy is 78.45 J·g-1 .