Preparation and Structure of PVDF Piezoelectric Film

Fu Wanli,DU Piyi,WENG Wenjian,HAN Gaorong

DOI: https://doi.org/10.3321/j.issn:1005-3093.2005.03.004

2005-01-01

Abstract:Piezoelectric and ferroelectric polymer film of PVDF was successfully prepared by dip-coating method. The phase status, crystal morphology and thickness of the film were characterized by XRD and SEM. Thin film with polar orthorhombic crystal, β phase, is formed when isothermal crystallization at 60℃; while non-polar monoclinic crystal, a phase, is formed at 150℃. β crystal in the film exhibits as typical spherical structure, and its diameter increases with increasing the film's thickness. Due to its loose stacking, large interspace and low compactness are formed in the film, which results in a thicker film. However, the size of the a crystal, mainly formed by two-dimension growth at higher temperature, shows basically unchanged when the thickness of film increases. A thinner film with smaller interspace and better compactness is finally formed due to the close contacting of a crystal.