Influences of Different Lactic Acid Conformation on Copolymer of Lactic Acid and Glycolic Acid Synthesized Via Direct Melt Copolymerization

WANG Zhao-yang,ZHAO Yao-ming,WANG Fang
DOI: https://doi.org/10.3969/j.issn.1673-2812.2005.02.005
2005-01-01
Abstract:Respectively using L-lactic acid (L-LA) and D,L-lactic acid (D,L-LA) as starting material, and via direct melt copolycondensation with glycolic acid (GA), serial poly(lactic acid-glycolic acid) (PLGA) with different mol feed were synthesized after 10h's polymerization under 165℃ and 70Pa, and 0.5 wt% SnCl 2 as catalyst. These biodegradable polymers were characterized with GPC, FTIR, 1H NMR, DSC and X-ray diffraction. It was found that PLGA synthesized from L-LA and D,L-LA have many differences in Mw, Tg, crystallity and composition. When the mol feed ratio of LA to GA was 50/50, both the intrinsic viscosity ( [η] ) and weight-average molecular weight (Mw) of D,L-PLGA were higher than that of L-PLGA. Using D,L-LA as starting material, the structure of copolymer PLGA was relatively simple, and its properties were apt to be controlled by GA chain segment in copolymer. When the feed mol percentage of monomer (LA or GA) was more than or equal to 90%, the copolymer was apt to be crystalline, and the aptness was more obvious for L-LA monomer. The composition percentage of GA in PLGA was not only higher than the feed mol percentage of GA, but also the GA percentage in D,L-PLGA was higher than in L-PLGA. Based on the above, the copolymerization mechanism was proposed. The different monomers may have different reaction velocities, the reaction velocity of GA was quicker than that of L-LA, and that of D,L-LA was the slowest of three. Thus, when monomer GA respectively reacting with D,L-LA and L-LA, the reaction mechanism of direct melt copolycondensation was different..
What problem does this paper attempt to address?