Wear and Corrosion Resistance of AISI 316 Austenitic Stainless Steel After Plasma Source Nitriding Treatment

Guang-yu LI,Ming-kai LEI

DOI: https://doi.org/10.16577/j.cnki.42-1215/tb.2017.02.003

2017-01-01

Abstract:AISI 316 austenittc stainless steel was modified by plasma source nitriding technique under 450 ℃ for 6 h,and the single facecentered-cubic phase (γN) modified layer with thickness of 17 μm,20％ (atom fraction) peak value of N content and maximum microhardness of 1 510 HV0.1 N was obtained.WTM-2E ball-disc abrading instrument and PARSTAT2273 electrochemical workstation were utilized respectively to study the tribological behavior of γN phase/Si3N4 ceramic counterface under dry friction condition and the electrochemical corrosion behavior in 3.5％ NaC1 solution,which could further reveal wear and corrosion mechanism of γN phase.Results showed that the wear mechanism of γN phase modified layer changed from adhesion wear of original stainless steel to oxidation wear,and the friction factor decreased from 0.88 to 0.65,as well as the wear volume reduced from 0.13 mm3 to 9.50× 10-3 mm3,which indicated that the wear resistance was improved greatly.Furthermore,the pitting corrosion process of the γN phase modified layer was not observed from the anodic polarization curve,and the EIS of the γN phase passive film possessed a larger diameter of capacitive arc and wider phase degree range.Calculated based onequivalent circuit Rs-(Rct//CPE),the fitting charge transfer resistance Rct increased from 1.006× 105 Ω · cm2 of original stainless steel to 1.377×106 Ω · cm2,and the calculated double layer capacitance Cdl decreased from 88.4 mF/cm2 to 77.8 mF/cm2,which demonstrated that the corrosion resistance was enhanced.