Power Modulation Laser-MIG Hybrid Welding Process for 8 mm Thick T2 Pure Copper Plate

NING Jie,ZHANG Lin-jie,ZHANG Jian-xun

DOI: https://doi.org/10.3969/j.issn.1674-6457.2020.01.016

2020-01-01

Abstract:This paper aims to research interactive effect between welding parameters and modulation parameters on the thermal efficiency and stability of power modulation fiber laser-MIG hybrid welding for T2 pure copper. The ternary quadratic regression orthogonal tests on average power, wire feed rate, modulation amplitude and modulation frequency were designed and carried out. The melting area of base metal was used to characterize the thermal efficiency during welding, and the number of pores in the weld seam was used to characterize the stability during welding. The results showed that when the modulation amplitude was about 1/3 of the average power, the melting area of the base metal reached the largest, suggesting that the thermal efficiency of the welding process was the highest. The increase or decrease of the amplitude would reduce the melting area of base metal. The average power mainly determined the line energy of the welding process. The increase of average power would lead to the increase of melting area of the base metal. The wire feed rate not only affected the energy input of the welding process, but also had a great influence on the flow behavior of the molten pool. When the wire feed rate was too large, the molten pooland the small holes may be unstable, resulting in the instability of the welding process. Therefore, the wire feed rate should not be too large. In this study, it should be 10 m/min. The results of this paper show that the thermal efficiency and stability of 8 mm thick pure copper welding can be improved simultaneously by power modulation laser-arc hybrid welding with optimized process parameters and modulation parameters.