Microstructure and Mechanical Property of Mg-Gd-Y-Zr Magnesium Alloy Piston

HU Mao-liang,JI Ze-sheng,WANG Qu-dong,ZHU Yao,XU Hong-yu

DOI: https://doi.org/10.3969/j.issn.1674-6457.2016.04.014

2016-01-01

Abstract:In order to study microstructure and mechanical property of Mg-Gd-Y-Zr magnesium alloy piston body, this pa-per analyzed the microstructures of piston body that was produced by metal gravity casting under as-cast, solution treatment (T4) and aging treatment (T6) conditions by optical microscope and scanning electron microscope. It measured the mechanical prop-erties by Shimadzu tensile testing machine and hardness tester. As a result, the secondary phases were distributed along grain boundary in the as-cast Mg-Gd-Y-Zr microstructure of the piston and mostly dissolved into α-Mg matrix after T4 treatment. Amounts of the pitting-shaped and strip-shaped precipitation phases appeared in the grains after T6 treatment. The ultimate ten-sile strengths of piston skirt and piston top after T6 treatment decreased with increasing temperature. The ultimate tensile strength of piston skirt could reach 226.38 MPa at the tensile temperature of 300℃. The elongation of piston skirt and piston top increased with increasing temperature. At the tensile temperature of 350℃, the elongation of piston skirt could reach 23.65%. In conclusion, the ultimate tensile strength of magnesium alloy piston skirt at room temperature and high temperature is higher than that of piston top, and the grain size of piston skirt is relatively uniform.