Abstract:Silane coupling agent (KH-570) was used as modifying agent to modify apatite (HA-TCP). Porous HA-TCP/CS biomaterial was prepared by vacuum freeze-drying method. Analyses of the composite were carried out by means of XRD, SEM, TEM, IR and so on. Influence of the amount of coupling agent KH-570 on the relationship between compressive strength and porosity of the porous biomaterial was investigated. The results showed, compressive strength of the porous biomaterial decreased with the increasing of the content of silane coupling agent, and then increased with further increasing of the content of silane coupling agent. Porosity of the porous biomaterial increased with the increasing of the content of silane coupling agent, and then decreased with further increasing of the content of silane coupling agent. Matching of compressive strength and porosity of the porous biomaterial was the best when the mass ratio of HA-TCP to CS is 7:3, and the content of coupling agent KH-570 was 1wt% when compressive strength and porosity of the porous biomaterial were 4.1MPa and 83.8% respectively. The pore shape was stacking fault lath lapping and the distribution of pores is comparatively uniform. HA-TCP particles are uniformly dispersed on CS templates. The added coupling agent of KH-570 has little change on the phase structure of the material, only the intensity of characteristic diffraction peaks in each phase of the material have a little enhancement. The joining mechanism of silane coupling agent is that the -OH in structure could produce firm bonding action with the -OH in the surface of HA-TCP after the decomposition of KH-570. The double bond on the other side of the coupling agent could make the modificative HA-TCP powder more active in the combination with CS. The combination could bridge apatite and CS.

Study on the Interfacial Interaction Between Γ-(Trimethoxysilyl) Propyl Methacrylate and Nano-Apatite

Interface and Surface Properties of Nano-hydroxyapatite /poly (1,4-Phenylene-sulfide)-poly(2,4-phenylene Sulfide Acid) Copolymer Composite

Molecular Modification of Hydroxyapatite to Introduce Interfacial Bonding with Poly (lactic Acid) in Biodegradable Composites

Studies of surface functional modification of nanosized α-alumina

Interaction of silane coupling agents with nano-silica probed by nano-IR*

Aminopropyltriethoxysilane-mediated Surface Functionalization of Hydroxyapatite Nanoparticles: Synthesis, Characterization, and in Vitro Toxicity Assay.

XPS studies of Hydroxyapatite Powders by Grafting Octadecyltrichlorosilane

Utilization of functionalized silane coatings for enhanced mechanical properties of hydroxyapatite filler

A study on nano-composite of hydroxyapatite and polyamide

Effect of Amino-, Methyl- and Epoxy-Silane Coupling As a Molecular Bridge for Formatting a Biomimetic Hydroxyapatite Coating on Titanium by Electrochemical Deposition

Preparation and Characterization of Nano-Hydroxyapatite/silicone Rubber Composite

MODIFICATION OF APATITE/CHITOSAN POROUS MATERIALS WITH SILANE COUPLING AGENT

INTERFACIAL MODIFICATION OF QUARTZ FIBER REINFORCED SILICON-ARYLACETYLENE-CONTAINING RESIN COMPOSITE BY COUPLING AGENT

Surface modification of hydroxyapatite with poly(methyl methacrylate) via surface-initiated ATRP

Effect of Methyl and Hydroxyl Functional Group Surfaces on Crystallization of Hydroxyapatite Coating

Surface Functional Modification of Nanosized α-Alumina and Its Characterisation

Treatment of N-Ha Slurry and Composition of N-Ha/peek

Competition of Hydrolysis, Self-Polymerization and Graft Coupling for N-Dodecyltrimethoxysilane Modified Al2O3 under Non-Catalytic Conditions

Preparation of Nano-Ha/pla Composite by Modified-Pla for Controlling the Growth of HA Crystals

The Study on Preparation and Interface of N-Ha/poly (amino Acid) Composite

A Novel Preparation Method for Nano-HA/PLA Composite with Grafted PLA