Abstract:Creep-fatigue interaction is identified as a primary failure mode for components operating under high temperatures. As operational durations extend, this interaction not only alters the material's microstructures but also initiates a gradual degradation in mechanical properties, significantly impacting its deformation and damage behaviors. In this work, the dynamic microstructural evolution of GH4169 superalloy during creep-fatigue was elucidated via qualitative characterization, and damage level evaluation method was subsequently developed by bridging microstructure degradation to mechanical property degradation. Creep-fatigue tests were performed at 650 °C with various tensile holding times and were interrupted at lifetime fractions of 10 %, 50 % and 80 % for further analysis and tensile evaluations. Results revealed that the prolonged exposure to holding times induced the coarsening of γ″ precipitates alongside an increase in low-angle grain boundaries, culminating a reduction in creep-fatigue strength. The development of voids and cracks exacerbated the degradation of elongation, leading to a hybrid fracture mode encompassing both intergranular and transgranular cracking paths. Synthesizing microstructural evolutions to qualitatively categorize diverse degradation levels imparted a robust physical basis for damage evaluation. A mapping model was established to correlate the average kernel average misorientation (micro-degradation indicator) with the tensile plastic strain energy density (macro-degradation indicator). The damage level evaluation method was endowed with quantitative metrics utilizing this model, and its generality was additionally validated in P92 steel. This work offers an insight into the quantitative damage evaluations of creep-fatigue-induced degradations in materials, thereby providing a theoretical basis for the development of operation management and inspection plans of components.

Evaluation of creep damage in Ti60 alloys by nonlinear Lamb waves

Creep Damage Evaluation of Titanium Alloy Using Nonlinear Ultrasonic Lamb Waves

Creep Damage Characterization Using Nonlinear Ultrasonic Guided Wave Method: A Mesoscale Model

Creep Damage Evaluation of P92 Steels Using Nonlinear Lamb Waves

Lamb Wave Mode and Frequency Selection for Assessment of Creep Damage in Titanium Alloy Plates

Creep degradation characterization of titanium alloy using nonlinear ultrasonic technique

Effect Of Precipitate-Dislocation Interactions On Generation Of Nonlinear Lamb Waves In Creep-Damaged Metallic Alloys

Creep-Fatigue Behavior and Crack Analysis of Ti-6Al-4V ELI

Creep Damage Evaluation of Steam Turbine Rotor Steel by Using the Nonlinear Ultrasonic Technique

Experimental study of thermal degradation in ferritic CrNi alloy steel plates using nonlinear Lamb waves

Evaluation of Thermal Degradation Induced Material Damage Using Nonlinear Lamb Waves

Research on Fatigue-Creep Interaction Damage of Steel 1.25Cr0.5mo

A new creep damage assessment method for metallic material under variable load conditions at elevated temperature

Influence of Cyclic-Loading Induced Fatigue Micro-Crack Growth on Generation of Nonlinear Ultrasonic Lamb Waves

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Creep-fatigue Damage Level Evaluation Based on the Relationship Between Microstructural Evolution and Mechanical Property Degradation

Evaluation of Material Damage Using Nonlinear Ultrasonic Wave

In Situ Monitoring of High-Temperature Creep Damage in CrMoV High-Strength Structural Steel Using Acoustic Emission

Experimental and theoretical study on high-temperature creep of VT6 titanium alloy under multi-axial loading conditions

Evaluation of fatigue and creep-fatigue damage levels on the basis of engineering damage mechanics approach

Investigation on Characteristics of Tensile Damage and Microstructure Evolution of Steel AISI 316L by Nonlinear Ultrasonic Lamb Wave