Effect of Cr Contents on Microstructure and Mechanical Properties of ( TiBw + TiCp)/(Ti-4.0Fe-7.3Mo-xCr) Composites
Zhou Rui,Jia Dechang,Yang Yi,Yang Zhihua,Zhou Yu
DOI: https://doi.org/10.3969/j.issn.0258-7076.2012.04.008
2012-01-01
Abstract:Titanium alloys had a wide application as their good toughness and strength, but these alloys had relatively low abrasion resistance as the low hardness which limited their application as structure parts. The titanium matrix composites, 10% (TiB w+TiC p)/(Ti-4.0Fe-7.3Mo-xCr) composites with TiB:TiC=1:1, were prepared by in situ reaction between B 4C, C, Cr 3C 2 and titanium powders. The mixtures were hot pressed at 1300°C, under a pressure of 20 MPa for 1 h in Ar atmosphere. Microstructure and mechanical properties of the composites were investigated. The results showed that by changing the proportions of Cr 3C 2, B 4C, and C, the content of Cr from Cr 3C 2 could affect both the matrix and reinforcing phase. The composite was comprised of the α-Ti and β-Ti phase, and the content of β-Ti phase increased with the content of Cr from Cr 3C 2 increased by in situ reaction. With the increase of Cr content from Cr 3C 2 varied from 2.2% to 5.2%, the strength increased significantly, up to 908.7 MPa, while the Young's modulus decreased from 170 to 150 GPa, but the hardness (HRC) of the TMCs was much higher than that of the matrix alloy and remained steadily at 55. Additionally, the introduction of Cr 3C 2 could also influence the distribution and morphology of in situ formed TiB w and TiC p reinforcements. With the increase of Cr content from the Cr 3C 2, the aspect ratio of the TiB w rose, and the granularity of the TiC p declined which enhanced the strength and toughness of the composites.