Microstructure, magnetic properties and power loss characteristics of Mg1-xCuxFe2O4ferrites

Xian WANG,Jun-nan LI,Hui LUO,Shuo-qing YAN,Ze-kun FENG,Rong-zhou GONG
DOI: https://doi.org/10.3969/j.issn.1001-3830.2015.06.004
2015-01-01
Abstract:Polycrystalline Mg1-xCuxFe2O4(x=0, 0.4, 0.6 and 0.8) were prepared using solid-state reaction technique. The structure and static magnetic properties of the samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and vibrating sample magnetometer (VSM). Furthermore, the permeability, quality factor and core loss were measured within 10 kHz-1 MHz. The results indicate that the sintered Mg1-xCuxFe2O4 ferrites withx= 0~0.6 show a single-phase cubic spinel structure, but the sample withx = 0.8 exhibits an another phase with tetragonal structure. Moreover, it is observed that both grain size and density substantially increase with increasingx, whereas the resistivity shows a decrease. The saturation magnetization of the samples gradually increases from 20.7 Axm2/kg (x=0) to 30.4 Axm2/kg (x=0.8), while the coercivity decreases initially, reaches a minimum value of 445.7 A/m atx=0.6, and then increases with further increase in Cu content. A proper Cu2+ substitution for Mg2+ in the Mg1-xCuxFe2O4ferrites can improve the magnetic permeability and decrease the quality factor. Accordingly, the Cu-doped MgFe2O4 ferrites exhibit a significant increase in the core loss. At the frequency of 370 kHz, the Mg0.4Cu0.6Fe2O4ferritecan realize relatively high loss under an AC magnetic flux density below 20 mT.
What problem does this paper attempt to address?