Effects of Bauxite on Property of Al2O3-SiO2 Plastic Refractory

Xudong Luo,Guodong Zhang,Zhipeng Xie,Baochao Liu

DOI: https://doi.org/10.3969/j.issn.1000-8098.2015.01.009

2015-01-01

Abstract:Al2O3-SiO2 plastic refractory was produced with raw materials including four kinds of bauxites with different content of Al2O3, SiO2 powder and Al2O3 powder, Al(H2PO4)3/H3PO4 and calcium aluminate cement as binding agent and coagulant, through the process of mixing, forming, curing, drying and so on. The effect of bauxite with different content of Al2O3 on bulk density, strength at room temperature, linear change rate, wear resistance, phase composition and microstructure in matrix of plastic refractories that were dried and burned at 1100℃ respectively was studied through the introduction of different grade of bauxite in the plastic refractories. The results show that the bulk density of Al2O3-SiO2 plastic refractory dried and burned will increase with Al2O3 content in bauxite(meaning that the grade of bauxite was developed), which followed that the strength will decrease at room temperature. The crystalline characterization of corundum will be strengthened with bauxite grade being developed in the formula. The sintering aid of plastic refractories can be played by the impurities in bauxite and the calcium aluminate cement. The increasing Al2O3 in bauxite will increase the strength of aggregate particle, will reduce the sintering of the matrix, and will result that the strength match between the matrix and aggregate of plastic refractories will be weakened, which increases the amount of wear, and reduces the wear resistance.