Abstract:Porous hollow silica particles possess promising applications in many fields, ranging from drug delivery to catalysis. From the synthesis perspective, the most challenging parameters are the monodispersity of the size distribution and the thickness and porosity of the shell of the particles. This paper demonstrates a facile two-pot approach to prepare monodisperse porous-hollow silica particles with uniform spherical shape and well-tuned shell thickness. In this method, a series of porous-hollow inorganic and organic-inorganic core-shell silica particles were synthesized via hydrolysis and condensation of 1,2-bis(triethoxysilyl) ethane (BTEE) and tetraethyl orthosilicate (TEOS) in the presence of hexadecyltrimethylammonium bromide (CTAB) as a structure-directing agent on solid silica spheres as core templates. Finally, the core templates were removed via hydrothermal treatment under alkaline conditions. Transmission electron microscopy (TEM) was used to characterize the particles′ morphology and size distribution, while the changes in the chemical composition during synthesis were followed by Fourier-transform infrared spectroscopy. Single-particle inductively coupled plasma mass spectrometry (spICP-MS) was applied to assess the monodispersity of the hollow particles prepared with different reaction parameters. We found that the presence of BTEE is key to obtaining a well-defined shell structure, and the increase in the concentration of the precursor and the surfactant increases the thickness of the shell. TEM and spICP-MS measurements revealed that fused particles are also formed under suboptimal reaction parameters, causing the broadening of the size distribution, which can be preceded by using appropriate concentrations of BTEE, CTAB, and ammonia.

SYNTHESIZED OF MESOPOROUS SILICA HOLLOW SPHERES WITH N-MYRISTOYLALANINE AS THE TEMPLATE

Synthesis of mesoporous silica hollow spheres in supercritical CO2/water systems

Synthesis of Hollow Spheres with Mesoporous Silica Nanoparticles Shell

Facile Synthesis Of Monodisperse Microspheres And Gigantic Hollow Shells Of Mesoporous Silica In Mixed Water-Ethanol Solvents

Synthesis of Colloidal Mesoporous Silica Spheres with Large Through-Holes on the Shell

Synthesis of Hollow-Shell MCM-48 Using the Ternary Surfactant Templating Method

Synthesis of siliceous hollow spheres with large mesopore wall structure by supercritical CO2-in-water interface templating.

Preparation of hollow mesoporous silica spheres by a sol–gel/emulsion approach

Synthesis of Monodisperse Silica Microspheres with Solid Core and Mesopore Shell

Synthesis of Porous Hollow Organosilica Particles with Tunable Shell Thickness

Core-template-free Synthesis of Molecularly Ethane-Bridged Hollow Mesoporous Silica Spheres from Acid-Hydrolyzed Precursor

Mesoporous Silica Hollow Spheres with Ordered Radial Mesochannels by a Spontaneous Self-Transformation Approach

Synthesis of Hollow Mesoporous Silica Spheres with Radially Aligned Mesochannels and Tunable Textural Properties

One-Step Synthesis of Cagelike Hollow Silica Spheres with Large Through-Holes for Macromolecule Delivery.

Asymmetric PSt-EA/Ni-Silicate Hollow Microsphere with a Hierarchical Porous Shell

Facile preparation of silica hollow microspheres by precipitation-phase separation method

Template-assisted Synthesis of Mesoporous LiAlO2 Hollow Spheres with High Surface Area

Synthesis and Investigation of Hollow SiO_2 Nanospheres

Synthesis of Siliceous Hollow Spheres with Ultra Large Mesopore Wall Structures by Reverse Emulsion Templating

Facile synthesis of diamine-functionalized hollow mesoporous silica sphere with self-templating method

Novel and feasible method for synthesis of monodispersed hollow silicon dioxide submicrospheres