Abstract:Nano-ZSM-5 with large amount and high strength of acid sites were successfully synthesized by hydrothermal crystallization of pure-silica nucleus in NaAlO2 alkali solution. The concentration of NaAlO2 alkali solution was decreased by increasing the H2O/Al ratio from 200 to 2600, which strongly determined the acidic properties and crystal size of the obtained nano-ZSM-5. Low concentration of NaAlO2 alkali solution was found unfavorable for the incorporation of Al into the bulk of ZSM-5 crystal in crystallization process. Hence, more Al distributed at the exterior of crystals, which enhanced the accessibility of the acid sites during reaction. Large amount and high strength of acid sites were produced for nano-ZSM-5 by increasing H2O/Al ratio. When the H2O/Al ratio increased from 200 to 2600, the total amount of acid sites increased from 0.59 to 0.81 mmol g(-1), much higher than conventional value of 0.50 mmol g(-1). In addition, the acid strength increased and the ratio of Bronsted/Lewis acid sites were sharply increased from 2.3 to 4.1 when the H2O/Al ratio increased. Moreover, the size of nano-crystal was also decreased by above decreasing the concentration of the NaAlO2 alkali solution. When the H2O/Al ratio was 2600, the obtained sample possessed total acid amount of 0.81 mmol g(-1) and crystal size of 60 nm, respectively. Methanol to hydrocarbon (MTH) reaction results showed that the increased acid sites of the catalyst decreased its catalytic lifetime to some extent, but the aromatics selectivity was tunable obviously. As for the catalyst prepared with H2O/Al ratio of 2000, the aromatics selectivity of the obtained catalyst reached to 66.0%. This paper provided a method for the fabrication of small-size nano-ZSM-5 with large amount and high strength of acid sites and regulated Al distribution for MTH reaction.

Synthesis of nano-size HZSM-5 and their performances in MTP reaction

Direct synthesis of HZSM-5 zeolites with enhanced catalytic performance in the methanol-to-propylene reaction

EFFECT OF LONG CHAIN CATIONIC SURFACTANT ON ZSM-5 SYNTHESIS AND METHANOL TO OLEFIN REACTION

Synthesis of hierarchical ZSM-11 and its catalytic performances during methanol to propylene

Advances in Catalytic Conversion of Methanol to Propylene

Catalytic Study of Methanol-to-Propylene Conversion over Nano-Sized HZSM-5

Influence of framework Al distribution in HZSM-5 channels on catalytic performance in the methanol to propylene reaction

High-silica hierarchical ZSM-5 prepared by conventional alkali treatment: A highly stable MTP catalyst

Size controllable synthesis of ZSM-5 zeolite and its catalytic performance in the reaction of methanol conversion to aromatics

ZSM-5 Catalysts for MTO: Effect and Optimization of the Tetrapropylammonium Hydroxide Concentration on Synthesis and Performance.

Effect of Preparation Method on the Catalytic Performance of HZSM-5 Zeolite Catalysts in the MTH Reaction

In-situ synthesis of hierarchical lamellar ZSM-5 zeolite with enhanced MTP catalytic performance by a facile seed-assisted method

High-performance HZSM-5/cordierite Monolithic Catalyst for Methanol to Propylene Reaction: A Combined Experimental and Modelling Study

Direct synthesis of Zn-incorporated nano-ZSM-5 zeolite by a dry gel conversion method for improving catalytic performance of methanol to aromatics reaction

Controllable Synthesis of Nano-Zsm-5 Catalysts with Large Amount and High Strength of Acid Sites for Conversion of Methanol to Hydrocarbons

Conversion of Methanol to Propylene over a High Silica B-HZSM-5 Catalyst

EFFECTS OF CRYSTAL SIZE AND PHOSPHORUS MODIFICATION OF ZSM-5 ZEOLITE ON ITS CATALYTIC PERFORMANCE IN THE CONVERSION OF METHANOL TO PROPYLENE

Facile synthesis of rodlike ZSM-5 zeolite microspheres and catalytic performance in methanol to propylene reaction

Three-step short-time temperature-programmed hydrothermal synthesis of ZSM-5 with high durability for conversion of methanol to propylene

The Effect of Crystal Sizes of HZSM-5 Zeolites in Ethanol Conversion to Propylene

Synthesis of ZSM-5 by crystal seed-induced method and its application in methanol aromatization