Abstract:In the process of petroleum exploitation, in order to effectively inhibit the corrosion damage of acid to metal equipment. Mannich base corrosion inhibitors are generally added to inhibit the corrosion damage of acid. In order to enhance the solubility of Mannich base corrosion inhibitor. This paper intends to introduce hydrophilic groups to enhance the solubility of the Mannich base corrosion inhibitor. In this paper, two efficient corrosion inhibitors 3-(2-hydroxyethylamino)-1-phenylpropan-1-one (MY1) and 3-(2-aminoethylamino)-1-phenylpropan-1-one (MY2), were synthesized based on the Mannich reaction, using formaldehyde, acetophenone and ethanolamine/ethylenediamine as reaction raw materials. The corrosion inhibition performance of the inhibitor on N80 steel in 15% (mass fraction) hydrochloric acid solution was studied by means of the static weight loss method, electrochemical test and optical contact angle analysis. It could be seen from the static weight loss method that the corrosion rate in the hydrochloric acid solution before and after adding 0.7% (mass fraction) corrosion inhibitor concentration decreased from 129.39 g·m−2·h−1 to 1.45 g·m−2·h−1 and 2.79 g·m−2·h−1, respectively. The corrosion inhibition rate could reach 98%, indicating that both inhibitors had good corrosion inhibition performance, and the corrosion inhibition effect of MY1 was better than that of MY2. It was found from the electrochemical tests that the two inhibitors were mixed corrosion inhibitors mainly inhibiting the anodic reaction, and both inhibitors belonged to spontaneous adsorption, and their adsorption behaviors followed the Langmuir adsorption isotherm. In addition, the surface of N80 steel was characterized by SEM, EDS elemental mapping and contact angle measurement. The results show that a dense hydrophobic film is formed on the surface of the steel sheet after the addition of a corrosion inhibitor, which prevents corrosion.

Corrosion Inhibition Effect Research of Compound Corrosion Inhibitor for N80 Steel in HCl Solution Medium

Synergistic Effect Of Mannich Base And Sodium Tungstate As Corrosion Inhibition For N80 Steel

Corrosion Protection of N80 Steel in Hydrochloric Acid Medium Using Mixed C15H15NO and Na2WO4 Inhibitors

Inhibition Properties of Acidizing Corrosion Inhibitor for N80 Steel in Hydrochloric Acid

Corrosion and Inhibition of N80 Steel in 5% HCl Solution by SA1-3

Newly Synthesized Morpholinyl Mannich Bases As Corrosion Inhibitors for N80 Steel in Acid Environment.

Corrosion Inhibition of N80 Steel Using Novel Diquaternary Ammonium Salts in 15% Hydrochloric Acid

Anti-corrosion Performance of Composite Inhibitor for N80 Steel in NaIO4 Solution

Two Schiff Base As Corrosion Inhibitors for N80 in 1.0 M HCl: Experimental and Theoretical Studies

The effect of N and S ratios in N, S co-doped carbon dot inhibitor on metal protection in 1 M HCl solution

Synthesis of a Hydroxyl-Containing Corrosion Inhibitor and Its Inhibitory Performance on N80 Steel in Hydrochloric Acid Solution

Corrosion Inhibition of N80 Steel in 10% HCl+8% HBF4 Solution

3-(Diethylamino)-1-phenylpropan-1-one As a Corrosion Inhibitor for N80 Steel in Acidization of Petroleum Exploitation

Corrosion Inhibition of Kudingcha Extract for N80 Steel

Corrosion Inhibition of N80 Steel in 10% Citric Acid +1% Hf Solution

Synthesis and Anti-Corrosion Performance of C21H25NO on Corrosion of N80 Steel in Hydrochloric Acid Solution

EFFECT OF CHLORIDE ION ON CORROSION BEHAVIOR OF N80 STEEL IN CO2 SOLUTIONS

Bis-Mannich bases as effective corrosion inhibitors for N80 steel in 15% HCl medium

Investigation of some Porphyrin Derivatives as Inhibitors for Corrosion of N80 Steel at High Temperature and High Pressure in 3.5% NaCl solution containing carbon dioxide

Optimization and Evaluation of Corrosion Inhibitors for N80 Steel in Sulfamic Acid Solutions

New Mechanism of Corrosion Inhibitor Compounding Mannich Base and Na2WO4