Research on Hydrothermal Iron Removal From Wet Zinc Refining Solutions and Iron Residue Reduces Emissions
Changwen Li,Jianqing Song,Cunxiong Li,Qiang Liu,Zhihui Gu,Qiliang Wang,Kefeng Ye
DOI: https://doi.org/10.1080/10584587.2024.2324677
2024-10-25
Integrated Ferroelectrics
Abstract:For the conventional wet zinc refining processes of the jarosite method and goethite method of iron removal, the process that existed was iron residue low iron, high zinc, large amount of residue, and high cost of harmless treatment, this paper carried out a study on hydrothermal iron removal from wet zinc refining solutions and an iron residue that reduces emissions. The results show that the reaction temperature is a prerequisite for the precipitation of Fe 3+ to precipitate hematite (Fe 2 O 3 ). Prolonging the reaction time can induce the conversion of jarosite (KFe 3 (SO 4 ) 2 (OH) 6 ) to hematite. Increasing the partial pressure of oxygen will accelerate the oxidation of Fe 2+ to Fe 3+ and promote the formation of the hematite phase. Under the optimized technical parameters of reaction temperature 180 °C, oxygen partial pressure 0.6 MPa, reaction time 3 h, and controlled alkali metal ion concentration, 92.49% of the iron in the solution was precipitated into the residue in the form of hematite(Fe 2 O 3 ), and the precipitated iron residue contained 57.75% iron and 0.82% zinc; compared with the jarosite process, the amount of iron residue was reduced by about 65%, and the zinc content of iron residue was reduced by 5.86%. The use of hydrothermal mineralization iron precipitation processes can realize the mineralization precipitation of iron in solution under low-acid conditions and obtain hematite iron precipitation residue with iron content up to the industry standard of iron oxide. And can be realized for resource utilization, helping the wet process zinc industry to develop in a green and low-carbon direction.
engineering, electrical & electronic,physics, condensed matter, applied